微量铅和铬酸盐对高压铝箔腐蚀行为的影响

1.北京科技大学材料学系,北京,100083;新疆众和股份有限公司,新疆,乌鲁木齐,830013

2.北京科技大学材料学系,北京,100083

基金项目: 国家高技术研究发展计划(863计划)(2003AA32x170)

Influence of Micro-alloyed Pb and Chromate on the Corrosion Behavior of High Voltage Anode Aluminum Foil

研究了含微量铅和无铅高压阳极铝箔在铬酸系和非铬酸系溶液中的电化学腐蚀行为和对比电容的影响.用扫描电子显微镜观察了铝箔的腐蚀形貌.结果表明,重铬酸盐腐蚀和微量铅均可单独使高压阳极铝箔在腐蚀过程中发孔均匀,并提高比电容.相关的环保型高压铝箔生产技术还有待深入开展.

[1]	毛卫民.金属材料的晶体学织构与各向异性[M].北京:科学出版社,2002:116-118.
[2]	陈国光.曹婉真电解电容器[M].西安:西安交通大学出版社,1993:89-106.
[3]	曹婉真;徐友龙;袁战恒;邵祖发, 等.电解电容器阳极铝箔的腐蚀工艺[P].中国发明专利,ZL94118454 4,1994-12-01.
[4]	Chen N;MaoW;YuY;YangH, ZhangY.Amethod of quantitative fiber texture analysis[A].Beijing:Inter Acad Publisher,1996:81-83.
[5]	Ashitaka Z.;Skeldon P.;Wood G.C.;Shimizu K.;Thompson G.E. .Behavior of copper and lead during heat-treatment and surface treatment of aluminium capacitor foils[J].Journal of the Electrochemical Society,1999(4):1380-1385.
[6]	Lin W;Tu G C;Lin C F;Peng Y M .The effect of lead impurity on the DC-etching behavior of aluminum foil for electrolytic capacitor usage[J].Corrosion Science,1996,38:889-907.
[7]	毛卫民.高比电容低压阳极铝箔的表面微观组织[J].世界科技研究与发展,2004(03):16-21.

上一张下一张

计量

作者相关

文章评分