采用燃烧法,以稀土硝酸盐和二硫代乙二酰胺为反应物,在点燃温度为300-350℃时,制备了Gd2O2S:Tb3+X-射线纳米荧光粉.分别以X-射线衍射(XRD)、扫描电子显微镜(SEM)、光致发光(PL)光谱及X-射线激发的发光(XEL)光谱对样品进行了表征.XRD分析表明,当焙烧温度小于500℃时,可得到单一相的Gd2O2S:Tb3+X-射线纳米荧光粉;当温度为700℃时,样品完全转变为Gd2O2SO4相.SEM照片给出荧光粉具有疏松和多孔的块状及连续的三维的网络结构.PL和XEL光谱均呈现出激活剂Tb3+离子的较强的特征发射,但它们的峰位略有差别.此外,本实验Tb3+离子的最佳掺杂浓度是0.35mol%.
参考文献
| [1] | 孙家跃;杜海燕;胡文祥.固体发光材料[M].北京:化学工业社,2003:476. |
| [2] | T Justel;H Nikol;C Ronda .[J].Angewandte Chemie International Edition,1998,37:3085. |
| [3] | S Shionoya;W M Yen.Phosphor Handbool[M].CRC Press, Boca Raton, FL,1998 |
| [4] | Ravichandran D;Roy R;White BW .[J].Journal of the Society For Information Display,1997,5:107. |
| [5] | Ruan K S;Zhou G J;Zhong M A;Duan F J Yang B X Su Z M .[J].Journal of Alloys and Compounds,1998,72:275. |
| [6] | D Ma;X Liu;Y Pei;LCao.[J].San Jose CA USA Society for Information Display,1997:423. |
| [7] | M Ihara;T Igarashi;T Kusunoki;K Ohno .[J].Journal of the Electrochemical Society,2002,149H:72. |
| [8] | Blasse G;Bril A .[J].Philips Research Reports,1967,22:481-504. |
| [9] | BlasseG;Bril A .[J].Journal of Chemical Physics,1967,47(12):5139-5145. |
| [10] | 饶海波,成建波,杨开愚,黄宗琳.红色显示用单晶荧光体[J].光学学报,1999(05):683-688. |
| [11] | 饶海波,成建波,黄宗琳.Tb3+∶YAG单晶荧光层中掺杂Ga3+的荧光敏化作用[J].光学学报,2004(02):264-267. |
| [12] | Jungsik Bang;Mostafa Abboudi;Billie Abrams;Paul H. Holloway .Combustion synthesis of Eu-, Tb- and Tm- doped Ln_2O_2S (Ln = Y, La, Gd) phosphors[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2004(3/4):177-185. |
| [13] | Spurr RA;Myers H .[J].Analytical Chemistry,1957,29:760-762. |
| [14] | 欧阳芳平,唐波.Y2O2S：Tb纳米晶的能量传递过程的研究[J].稀有金属材料与工程,2003(07):522-525. |
| [15] | 祖成奎,陈洁.Tb3+激活硅酸盐玻璃的发光性能及其X射线转换屏应用研究[J].硅酸盐学报,2004(03):283-286,298. |
| [16] | Haykawa T .[J].Journal of Lu min,1997,72-74:925-926. |
| [17] | 李彬.Tb3+，Ce3+离子在Al6Si2O13中的光致发光[J].吉林大学自然科学学报,1996(03):87-90. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%