在0.3mol/dm3的草酸溶液中,采用二次阳极氧化法制备多孔氧化铝模板,研究了阳极氧化后的扩孔处理对多孔膜形貌和结构的影响.SEM和FE-SEM结果表明,经20min超声波扩孔处理后,多孔氧化铝模板纳米孔的结构更加趋于规则,表观孔径从30nm增大到70nm,其扩孔效果较常规扩孔方法更为明显.超声波扩孔时间增加到40min后,多孔膜孔径扩大至100nm,但某些区域的纳米孔壁已被部分溶解.在一定的电压范围内,随着电压增加,经超声波扩孔后的多孔氧化铝膜孔径增大,有序度有较大提高.
参考文献
| [1] | KellerF;Hunter M S;Robinsio D L .[J].Journal of the Electrochemical Society,1953,100:411. |
| [2] | Masuda H;Fukuda K .ORDERED METAL NANOHOLE ARRAYS MADE BY A TWO-STEP REPLICATION OF HONEYCOMB STRUCTURES OF ANODIC ALUMINA[J].Science,1995(5216):1466-1468. |
| [3] | 杨文彬,朱世富,赵北君,叶军,倪经,甄万宝,陈兴明.纳米孔阵列阳极氧化铝膜的制备和表征[J].无机化学学报,2003(04):366-370. |
| [4] | H Chik;J M Xu .[J].Materials Science and Engineering R:Reports,2004,43:103. |
| [5] | Li AP.;Birner A.;Nielsch K.;Gosele U.;Muller F. .Hexagonal pore arrays with a 50-420 nm interpore distance formed by self-organization in anodic alumina[J].Journal of Applied Physics,1998(11):6023-6026. |
| [6] | Masuda H.;Nishio K.;Yasui K. .Fabrication of ordered arrays of multiple nanodots using anodic porous alumina as an evaporation mask[J].Advanced Materials,2000(14):1031-1033. |
| [7] | ZHENG M;ZHANG L;ZHANG X;ZHANG J LI G .[J].Chemical Physics Letters,2001,334:298. |
| [8] | ZHANGX;ZHANG L;CHEN W;MENG G, ZHENG M, ZHAO L .[J].CHEMISTRY OF MATERIALS,2001,13:2511. |
| [9] | Wan DY;Wang YT;Zhou ZP;Yang GQ;Wang BY;Wei L .Fabrication of the ordered FeS2 (pyrite) nanowire arrays in anodic aluminum oxide[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2005(2):156-159. |
| [10] | Zhou YK.;Huang J.;Shen CM.;Li HL. .Synthesis of highly ordered LiNiO2 nanowire arrays in AAO templates and their structural properties[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):260-267. |
| [11] | YuChengSui;Jose MSaniger .[J].Materials Letters,2001,48:127-136. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%