运用乙醇湿法混合和氩气保护原位反应高温热压方法制备了不同配比的SiCp/MoSi2复合材料,研究了原位生成的SiC颗粒对MoSi2基体材料显微结构和室温力学性能的影响.结果表明:原位反应高温热压制备SiCp/MoSi2的工艺是可行的,反应生成的适量SiC颗粒细化了基体晶粒,改善了其力学性能;与该工艺下制备的纯MoSi2相比,含40vol%SiCp的SiCp/MoSi2复合材料室温抗弯强度提高了260%,含50vol%SiCp的SiCp/MoSi2复合材料室温断裂韧性提高了50%;该种工艺的强化机制为细晶强化和弥散强化,韧化机制为细晶韧化.
参考文献
| [1] | Vasudevan A K;Petrovic J J A .Comparative overview of molydbenum disilicide composite[J].Materials Science and Engineering,1992,155A:1-17. |
| [2] | 马勤;杨延清;康沫狂 .MoSi2及其复合材料的应用及展望[J].材料导报,1997,11(02):61-64. |
| [3] | Yang J M;Jeng S M .Interface and mechanical behavior of MoSi2-based composites[J].Materials Research,1991,6(03):505-513. |
| [4] | 金志浩,李世斌,高积强.MoSi2基复相材料的研究进展[J].西安交通大学学报,2001(02):199-202. |
| [5] | Costa e Silva A;Kaufman M J .In-Situ Formation of Alumina Coating in Niobium Toughened Mo(Si,A1)2[J].Scripta Metallurgica et Materialia,1994,31(07):853. |
| [6] | Costa e Silva A;Kaufman M J .Applications of In Situ Reaction to MoSi2-Based Materials[J].Materials Science and Engineering,1995,A195:75. |
| [7] | 马勤;杨延清;康沫狂 .原位技术在MoSi2基复合材料制备中的应用与发展[J].兵器材料科学与工程,1997,20(05):66. |
| [8] | 寇开昌,杨延清,艾云龙,陈彦,康沫狂.MoSi2-WSi2复合体系的自蔓延燃烧合成[J].稀有金属材料与工程,2000(03):190-192. |
| [9] | 张来启,孙祖庆,张跃,杨王玥,陈光南.原位SiC颗粒增强MoSi2基复合材料的显微组织和力学性能[J].金属学报,2001(03):325-331. |
| [10] | Zhang Laiqi;Sun Zuqing et al.Densification of MoSi2/SiCp composites and their microstructure[J].J Beijing University of Science and Technology,1997,19(06):577-579. |
| [11] | 孙岚,潘金生,清华大学,北京.TiC颗粒增韧MoSi2基复合材料的力学性能[J].材料工程,2001(09):31-34. |
| [12] | 郜剑英,江莞,李建林,吴历斌.二硅化钼合金化及掺杂改性的研究进展[J].中国钼业,2003(04):22-27. |
| [13] | Aikin R M .Strengthening of discontinuously reinforced MoSi2composites at high temperatures[J].Materials Science and Engineering,1992,155A:121-133. |
| [14] | Bhattacharya A K;Petrovic J J .[J].Journal of the American Chemical Society,1991,74:2700. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%