本文利用单辊法快速凝固技术制备了Mg-Zn-Nd合金薄带,并借助OEM、XRD、SEM等手段对其组织及性能进行了检测与分析.结果表明:快速凝固技术可显著优化Mg-Zn-Nd合金的组织结构与性能;薄带的凝固组织分为细晶区、柱状晶区、等轴晶区三个区域,保留了铸态凝固组织的特性;快速凝固技术的细晶强化和固溶强化可明显改善Mg-Zn-Nd合金的强度与塑性.本文研究的快速凝固镁合金系目前还未见报道,可为开发新型非平衡凝固条件下的镁合金系提供参考.
参考文献
| [1] | 夏德宏,郭梁,余涛.镁与镁合金广阔的应用前景[J].金属世界,2005(02):47-48. |
| [2] | 程天一;章守华.快速凝固技术与新型合金[M].北京:宇航出版社,1990:227-228. |
| [3] | Y Li.Critical cooling rates for glass formation in mgnind alloy[J].Journal of Non-Crystalline Solids,1994(175):224-227. |
| [4] | Y.L REN;J.H. ZUO;K.Q. QIU .Eutectic structure and bulk glass formation in Mg-based alloys[J].Intermetallics,2004(10/11):1205-1209. |
| [5] | X.K. Xi;D.Q. Zhao;M.X. Pan .On the criteria of bulk metallic glass formation in MgCu-based alloys[J].Intermetallics,2005(6):638-641. |
| [6] | Makoto Matsuura;Masaki Sakurai;Kenji Amiya .Local structures around Zn and Y in the melt-quenched Mg_(97)Zn_1Y_2 ribbon[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(1/2):240-245. |
| [7] | 陈吉华,陈振华,严红革.快速凝固镁合金的研究进展[J].化工进展,2004(08):816-822. |
| [8] | P.M. Jardim;G. Solorzano;J.B. Vander Sande .Second phase formation in melt-spun Mg-Ca-Zn alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):196-205. |
| [9] | D. Y. Maeng;T. S. Kim;J. H. Lee;S. J. Hong;S. K. Seo;B. S. Chun .Microstructure and strength of rapidly solidified and extruded Mg-Zn alloys[J].Scripta materialia,2000(5):385-389. |
| [10] | 刘正.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002:53. |
| [11] | W B Pearson.AHandbook of Lattice Spacings and Structure of Metals and Alloys[M].Pergamon,London,1958:177. |
| [12] | 胡德林.金属学及热处理[M].西安:西北工业大学出版社,1995:220. |
| [13] | 徐锦锋,翟秋亚,袁森.AZ91D镁合金的快速凝固特征[J].中国有色金属学报,2004(06):939-944. |
| [14] | 黄伯杰,聂邦盛,贾延杰,吴雅琴.Mg-Nd-Zn-Zr耐热高强铸造镁合金[J].特种铸造及有色合金,1998(06):40-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%