利用X射线衍射分析AOD渣的矿物组成,采用电子显微镜观察AOD渣的显微形貌,采用偏/反两用研究型显微镜观察AOD渣矿物相的嵌布特征.结果表明:AOD渣的主要物相为硅酸二钙、镁硅钙石、辉石、硅钙石及少量的尖晶石、磁铁矿以及微量的富氏体、玻璃相、RO相和铁酸钙;硅酸二钙体积分数达80％以上,镁硅钙石、辉石、硅钙石体积分数分别为5％左右;硅酸二钙和硅钙石为黑色相,硅酸二钙呈细小粒状集合体、柱状,粒度粗细不等;硅钙石呈他形晶、细小柱状;镁硅钙石存在于灰色相,主要呈他形粒状、细小纺锤状、短柱状;辉石、尖晶石和RO相包裹于优势相中,辉石呈他形粒状,粗细不等.
参考文献
| [1] | 韩伟.不锈钢渣湿式处理工艺及在宝钢的应用[J].宝钢技术,2010(03):30-33. |
| [2] | Qiang Wang;Peiyu Yan;Jianwen Feng .A discussion on improving hydration activity of steel slag by altering its mineral compositions[J].Journal of hazardous materials,2011(2/3):1070-1075. |
| [3] | Kuo Y M;Wang J W;Wang W T;Tsai C H .Effect of water quenching and SiO2 addition during vitrification of fly ash Part 1:On the crystalline cbaracteristics of slags[J].Journal of Hazardous Materials,2008,152:994-1001. |
| [4] | Quanyuan Chen,D.C. Johnson,Lingyun Zhu,Menghong Yuan,C.D. Hills.Accelerated carbonation and leaching behavior of the slag from iron and steel making industry[J].北京科技大学学报（英文版）,2007(04):297-301. |
| [5] | 周玉;武高辉.材料分析测试技术[M].哈尔滨:哈尔滨工业大学出版社,2007 |
| [6] | 李安东;郑浩宇.不锈钢渣的污染特性和综合利用研究进展[A].,2011:659. |
| [7] | 石洪志;王如意;陈荣欢 等.不锈钢渣用作水泥混合材及其安全性分析[J].建筑材料学报,2010,12(13):803-805. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%