采用一次性液相硅浸渍法(LSI)制备低成本的Cf/C-SiC复合材料.以PAN基平板碳毡为增强体,在酚醛树脂溶液中添加碳化硅微粉,探讨添加碳化硅浓度、浸渍压力及保压时间等因素对一次液相浸渍效果的影响.通过显微分析,当压力为1.2 MPa,浸渍时间为60 min时,可以获得最大的致密度,最终复合材料密度达2.64 g/cm3.
参考文献
| [1] | Naslain R .Design,preparation and properties of non-oxide CMCs for application in engines and nuclear reactiors:an overview[J].Composites Science and Technology,2004,64:155-170. |
| [2] | Besmann T M;Lowden R A.Chemical vapor Infiltration[A].Pennington NJ:Electrochemical Society,1990:482-489. |
| [3] | Stinton D P;Caputo A J;Lowden R A .Synthesis of fiber-reinforced SiC composites by chemical vapor deposition[J].American Ceramic Society Bulletin,1986,64(02):347-350. |
| [4] | 张长瑞;陈朝辉 .先驱体转化法制备碳纤维增强碳化硅陶瓷基复合材料研究[J].复合材料学报,1994,11(03):26-31. |
| [5] | Kochendorfer R.Liquid silicon infiltration-a fast and low cost CMC manufacturing process[A].Honolulu:ICCM,1991:231-234. |
| [6] | 闫志巧,熊翔,肖鹏,黄伯云.MSI工艺制备C/SiC复合材料的氧化动力学和机理[J].无机材料学报,2007(06):1151-1158. |
| [7] | 朱云洲,黄政仁,董绍明,袁明,江东亮.C/SiC复合材料的常压制备与性能研究[J].无机材料学报,2007(04):685-689. |
| [8] | 谢翀博,徐永东,王毅,张立同,成来飞,王一光,童长青.3D碳纤维预制体中料浆浸渗引入SiC微粉工艺研究[J].航空材料学报,2008(04):88-93. |
| [9] | 余林,徐永东,张立同,成来飞,范尚武,晏瑜.树脂液相浸渍法制备3D针刺碳/碳预制体影响因素研究[J].玻璃钢/复合材料,2007(04):26-29,41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%