以无机盐-硝酸氧锆为原料,采用醇-水加热-超临界干燥法制备了二氧化锆气凝胶.采用XRD、TEM和BET等手段对样品进行测试表征.研究结果表明:本方法可以制备具有高比表面、小粒径的二氧化锆气凝胶.气凝胶原粉的比表面最大,可达675.6m2/g.其晶相结构也不同于采用一般方法制备的ZrO2粉体.在焙烧温度低于700℃时,随着焙烧温度的升高,四方相的含量逐渐增大,到700℃时达到最大86%;经1000℃焙烧后尽管粒径＞30nm,仍有约30%的ZrO2以四方相的形式存在.探讨了醇水加热法制备ZrO2气凝胶的成胶机理.
参考文献
| [1] | Vartuli J C;Santiesteban J G;Traverso P et al.[J].Journal of Catalysis,1999,187(01):131-138. |
| [2] | Su Caili;He Dehua;Li Junrong et al.[J].Journal of Molecular Catalysis A:Chemical,2000,153(1-2):139-146. |
| [3] | Quaschning V.;Druska P.;Niclas HJ.;Kemnitz E.;Deutsch J. .Properties of modified zirconia used as Friedel-Crafts-acylation catalysts[J].Journal of Catalysis,1998(2):164-174. |
| [4] | Scheithauer M.;Gates BC.;Knozinger H.;Jentoft RE. .n-pentane isomerization catalyzed by Fe- and Mn-containing tungstated zirconia characterized by Raman spectroscopy[J].Journal of Catalysis,2000(2):271-274. |
| [5] | Stoker C;Baiker A .[J].Journal of Non-Crystalline Solids,1998,223:165-178. |
| [6] | 王远洋;吴东;樊彦贞 等.[J].物理化学学报,1997,13(07):580-585. |
| [7] | Moon Y T;Park H K;Kim D K et al.[J].Journal of the American Ceramic Society,1995,78:2690-2694. |
| [8] | Li W;Gao L;Guo J K .[J].Nano-Structured Materials,1998,10:1043-1049. |
| [9] | White J F .[J].Transactions A I Ch E,1942,38:435-439. |
| [10] | Garvie R C .[J].Journal of Physical Chemistry,1965,69:1238-1243. |
| [11] | Matjevic E .[J].Accounts of Chemical Research,1981,14:22-29. |
| [12] | 郑燕青,施尔畏,李汶军,陈之战,仲维卓,胡行方.水热反应条件二氧化锆同质变体的形成[J].中国科学E辑,2001(04):289-295. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%