利用光学显微镜(OM)、场发射扫描电子显微镜(FESEM)、电子万能试验机、数显洛氏硬度计和显微硬度仪研究微量Sr对镁合金AM60B的铸态组织和力学性能的影响.结果表明,添加微量元素Sr可以细化镁合金的晶粒,而不改变基体α-Mg相的枝晶形貌,但可改变γ相的形态和大小,从连续或断续网状、长条状,变为卵石状或颗粒状.Sr对AM60B镁合金的抗拉强度和延伸率的影响具有相似的趋势,即随着Sr含量的增加,合金的抗拉强度和延伸率呈现先升后降的趋势,当Sr含量为0.05%时抗拉强度和延伸率分别达到最大值191.82 MPa和4.63%,而洛氏硬度和显微硬度随着Sr含量的增加而增大.AM60B镁合金断裂方式存在着由解理断裂向准解理断裂再向解理断裂转化的模式.
Effects of trace element Sr on the as-cast microstructure and mechanical properties of magnesium alloy AM60B were studied by optical microscope (OM), field emission scanning electron microscopy (FESEM), electronic universal testing machine, digital display Rockwell hardness tester and microhardness tester. The results show that the addition of trace element Sr can refine grains without change of dendrite morphology of matrix α-Mg phase, but can change the morphology and size of γ-Mg_(17)A1_(12) phase from continuous/discontinuous netlike or strip form to cobble or particulate form. The effect of Sr on the tensile strength and elongation of AM60B magnesium alloy has the similar tendency, i.e. with the increase of Sr content, the tensile strength and elongation of AM60B magnesium alloy are first increased and then decreased. With addition of 0.05% Sr, the tensile strength and elongation reach the maximum 191.82 MPa and 4.63%, respectively, while the Rockwell hardness and microhardness are increased with the increase of Sr content. The fracture mechanism of AM60B magnesium alloy is changed from cleavage fracture to quasi-cleavage fracture to cleavage fracture.
参考文献
| [1] | 刘生发,王慧源.Sr对AZ91镁合金铸态组织的影响及其细化机制[J].稀有金属材料与工程,2006(06):970-973. |
| [2] | T Aliravci C A et al.[J].AFS Transactions,1992,115:353. |
| [3] | Lee Y C et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,31(11):2895. |
| [4] | 徐宋兵,彭晓东,陈刚,谢卫东.Mg-8Sr中间合金对AZ91晶粒细化的研究[J].轻合金加工技术,2005(10):29-32. |
| [5] | 郑飞燕,翁康荣,白慧龙,赵红亮,关绍康.微量Sr对AZ91D镁合金凝固过程的影响[J].特种铸造及有色合金,2006(11):745-746. |
| [6] | PAN Yichuan,LIU Xiangfa,YANG Hua.Sr Microalloying for Refining Grain Size of AZ91D Magnesium Alloy[J].武汉理工大学学报（材料科学版）（英文版）,2007(01):74-76. |
| [7] | 杨明波,潘复生,李忠盛,程仁菊.Sr对Mg-3Al-1Zn镁合金铸态组织的影响[J].重庆工学院学报（自然科学版）,2007(03):10-12. |
| [8] | 崔红卫,刘俊成,李红,高巧春.微量Sr对AZ91D的铸态组织和性能的影响[J].特种铸造及有色合金,2007(12):968-970. |
| [9] | 杨明波,程仁菊,潘复生,汤爱涛.Mg-9Sr中间合金的组织及其对AZ31镁合金组织细化的影响[J].稀有金属材料与工程,2008(03):413-417. |
| [10] | 金鑫焱,李双寿,曾大本,唐靖林.Sr对AM60B铸造镁合金晶粒细化的影响[J].铸造,2005(06):566-569. |
| [11] | 安阁英.铸件成形理论[M].北京:机械工业出版社,1990:22. |
| [12] | 龚丽勤,李建国,周鹏,王发奇,仝仲盛,陶占东.Al3Ti3B中间合金对AZ91D镁合金组织及力学性能的影响[J].中国有色金属学报,2004(12):2003-2008. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%