本文将固相法制备的磁损耗型Ba0.9Sm0.1Co2Fe16O27铁氧体与电损耗型石墨相结合,通过测试两者的电磁参数,采用YRcomputor软件模拟计算了双层复合吸波涂层的反射率。结果表明：铁氧体/石墨复合吸波涂层在2～8 GHz频段有较好的吸波性能;其中,下层为含量80 wt%的Ba0.9Sm0.1Co2Fe16O27,厚度1.5 mm,上层为10 wt%的石墨,厚度1.5 mm时,该复合涂层表现出优良的微波吸收特性,反射率损耗RL〈-10 dB时,带宽约为3 GHz（3.5～6.5 GHz）,最大吸收值约为-27 dB。
Magnetic loss-type Ba0.9Sm0.1Co2Fe16O27 ferrite prepared by the solid state method and electric loss-type graphite were combined,and the electromagnetic parameters were tested.In addition,the reflectivity of the double layer composite coating was successfully simulated by YRcomputor software.It is shown that the ferrite/graphite composite coating exhibited excellent microwave absorbing properties in 2 ~ 8 GHz band.When the lower layer was 80 wt% Ba0.9Sm0.1Fe12O19 with a thickness of 1.5 mm and the upper layer was 10 wt% graphite with a thickness of 1.5 mm,the composite coating showed great microwave absorbing properties.The maximum value of reflection loss（RL） was-27 dB,and the frequency width reached to 3 GHz（3.5 ~ 6.5 GHz） when RL was below-10 dB.
参考文献
| [1] | 黄娟娟 .片状磁性金属及合金纳米颗粒的微波磁性与微波吸收特性研究[D].兰州大学,2007. |
| [2] | 张晶 .共沉淀法制备纳米ATO粉末[D].南京:南京工业大学,2008. |
| [3] | 侯进 .水滑石、石墨、碳化硅以及铁氧体复合吸波涂层制备与性能研究[D].中国海洋大学,2007. |
| [4] | 沈国柱,徐政,张先如.铁氧体和碳纤维双层复合材料吸波性能研究[J].同济大学学报（自然科学版）,2008(03):379-382,401. |
| [5] | 沈国柱,徐政,蔡瑞琦.基于铁氧体和碳纤维的双层复合材料吸波性能研究[J].玻璃钢/复合材料,2007(01):19-23. |
| [6] | 于斌,齐鲁.多功能隐身材料的研究与应用现状[J].红外技术,2003(03):63-66. |
| [7] | 李金儡,陈康华,范令强,彭伟才,黄兰萍.雷达吸波材料的研究进展[J].功能材料,2005(08):1151-1154. |
| [8] | 刘献明,付绍云,张以河,孙正滨,李广涛.雷达隐身复合材料的研究进展[J].材料导报,2004(05):8-11. |
| [9] | 郭小芳,王长征,吴世洋.吸波材料的研究现状与发展趋势[J].甘肃冶金,2010(04):47-50,52. |
| [10] | 安莹莹.浅谈多层结构吸波复合材料[J].科技传播,2010(19):145-145. |
| [11] | 曾爱香,熊惟浩.纳米复合铁氧体微波吸收剂的研究进展[J].长沙电力学院学报(自然科学版),2003(04):72-76. |
| [12] | 赵德旭,李巧玲,张存瑞,李保东,赵静贤.碳纳米管/铁氧体/环氧树脂复合吸波材料的研究进展[J].塑料助剂,2009(06):5-10. |
| [13] | 吕淑珍,陈宁,王海滨,霍冀川.掺铁氧体和石墨水泥基复合材料吸收电磁波性能[J].复合材料学报,2010(05):73-78. |
| [14] | 张倩,焦清介,关晓存.纳米γ-Fe2O3/膨胀石墨复合材料制备及电磁性能[J].材料热处理学报,2010(07):30-33. |
| [15] | 李保东,李巧玲,张存瑞,赵静贤.铁氧体复合吸波材料研究新进展[J].材料导报,2008(z3):226-229. |
| [16] | 宋杰,许乃岑,王丽熙,张其土.Sm3+掺杂对MnZn铁氧体显微结构及性能的影响[J].电子元件与材料,2009(09):54-57. |
| [17] | Lixi Wang;Jie Song;Qitu Zhang .The microwave magnetic performance of Sm~(3+) doped BaCo_2Fe_(16)O_(27)[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):863-866. |
| [18] | 夏其英,马登学.纳米铁氧体复合涂料的制备及性能研究[J].临沂师范学院学报,2008(03):71-75. |
| [19] | 张存瑞,李巧玲,李保东,赵静贤.铁氧体/高分子纳米复合材料的制备方法及展望[J].合成技术及应用,2008(02):31-35. |
| [20] | 李元勋,刘颖力,张怀武,凌味未,谢云松,XIAO John-Qiang.聚苯胺钡铁氧体纳米复合材料的制备、表征及性能[J].高等学校化学学报,2008(03):640-644. |
| [21] | 熊为华,方庆清,王保明,王翠萍,周军,李貌.PANI/SrFe12O19复合材料的结构和吸波性能[J].磁性材料及器件,2007(03):30-32,45. |
| [22] | 朱正和.多层微波隐身材料反射系数的理论研究[J].战术导弹技术,2002(06):56-60. |
| [23] | 罗洁,徐国亮,蒋刚,刘波,朱正和.双层结构碳团簇型微波隐身材料的吸波性能研究[J].功能材料,2002(04):401-402. |
| [24] | 杨海波,林营.MnZn铁氧体/SrTiO3/PTFE复合材料的制备与表征[J].陶瓷,2007(04):22-24. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%