利用X射线应力测定仪采用不同的条件分别测定了304不锈钢薄壁焊管的表面轴向和切向残余应力,并研究了950℃保温30min水冷热处理前后其表面残余应力的变化。结果表明：采用铬靶Kβ辐射、2mm准直管测得的残余应力数据稳定且绝对误差小;热处理前薄壁焊管表面存在较大的残余拉应力,且焊管表面切向残余应力大于轴向残余应力;热处理后,表面拉应力变为压应力。
Axial and tangential surface residual stresses of 304 stainless steel thin-wall welded pipe were measured by X-ray stress tester through different methods.The surface residual stress change of the alloy before and after heat treated at 950 ℃ for 30 min and water cooling was studied.The results show that the data was stable and absolute error was small by the method of Cr Kβ and radiation 2 mm collimator.There was large residual tensile stress on the surface of the 304 stainless steel thin-wall welded pipe before heat treatment.And the tangential residual stress was greater than the axial residual stress.The surface residual tensile stress changed to compressive stress after heat treatment.
参考文献
| [1] | 梁成浩.奥氏体不锈钢的应力腐蚀破裂[J].石油化工设备,1986(03):19-25. |
| [2] | 龚利华,戴志仁.不锈钢热处理后表面氧化物的清洗研究[J].材料保护,2007(09):42-44. |
| [3] | 吕克茂.残余应力测定的基本知识--第四讲 X射线应力测定方法（三）[J].理化检验-物理分册,2007(09):462-468. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%