采用异丙基三(二辛基焦磷酸酰氧基)钛酸酯偶联剂对纳米羟基磷灰石(HA)改性,再与聚乳酸(PLA)/聚(3-羟基丁酸酯-co-4-羟基丁酸酯)(PHA)熔融共混法制备PLA/PHA/HA纳米复合降解材料.利用流变仪对其流变行为进行了研究.结果表明,PLA/PHA基体在没有添加钛酸酯偶联剂和纳米HA时,基体储存模量G '和复数黏度η*随温度升高而逐渐降低;纯的纳米HA的加入可以提高PLA/PHA基体的储存模量G'和损耗模量G",然而,PLA/PHA/HA纳米复合降解材料引入钛酸酯偶联剂反而会使储存模量G '和损耗模量G"降低.当过量引入钛酸酯偶联剂会明显降低体系线性-非线性转变的临界应变.在190℃,PLA/PHA基体加入纯的纳米HA时,储存模量G '升高,引入钛酸酯偶联剂后,基体储存模量G'反而有一定降低,但所有样品至少在30min内能保持较稳定的线性粘弹行为.
参考文献
| [1] | Kumar, M.;Mohanty, S.;Nayak, S.K.;Rahail Parvaiz, M. .Effect of glycidyl methacrylate (GMA) on the thermal, mechanical and morphological property of biodegradable PLA/PBAT blend and its nanocomposites[J].Bioresource Technology: Biomass, Bioenergy, Biowastes, Conversion Technologies, Biotransformations, Production Technologies,2010(21):8406-8415. |
| [2] | Swetha, M.;Sahithi, K.;Moorthi, A.;Srinivasan, N.;Ramasamy, K.;Selvamurugan, N. .Biocomposites containing natural polymers and hydroxyapatite for bone tissue engineering[J].International Journal of Biological Macromolecules: Structure, Function and Interactions,2010(1):1-4. |
| [3] | 唐义祥,梁多平,楼白杨.聚丁二酸丁二醇酯／聚羟基烷酸酯熔融共混物的结晶及流变力学行为[J].高分子材料科学与工程,2012(06):28-31,35. |
| [4] | Suryanegara, L;Okumura, H;Nakagaito, AN;Yano, H .The synergetic effect of phenylphosphonic acid zinc and microfibrillated cellulose on the injection molding cycle time of PLA composites[J].Cellulose,2011(3):689-698. |
| [5] | 唐义祥,楼白杨,梁多平.聚丁二酸丁二酯/纳米高岭土共混体系结晶及力学性能研究[J].高分子学报,2011(05):516-521. |
| [6] | 陶友季,章自寿,麦堪成.PP/回收PET共混物的稳态流变行为[J].高分子材料科学与工程,2010(10):56-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%