采用大气等离子喷涂在镁合金AZ31B表面制备了可降解钙/磷涂层.利用XRD、SEM、EDS分析了涂层的相组成、结晶度及在人体模拟液(SBF)中浸泡前后的显微形貌和元素组成,根据pH值和降解速率研究了涂层的体外降解性能.研究表明:钙/磷涂层与镁合金基体紧密结合,致密度高,涂层由较难降解的HA相和较易降解的Ca3(PO4)2、Ca4P2O9和CaO组成,涂层中HA结晶度为49.3％.生物降解性能研究显示,钙/磷涂层材料在SBF溶液中的pH值和降解速率均小于镁合金基体,且较小的变化幅度使涂层材料的降解行为控制在稳定范围内.
参考文献
| [1] | Staiger MP;Pietak AM;Huadmai J;Dias G .Magnesium and its alloys as orthopedic biomaterials: A review[J].Biomaterials,2006(9):1728-1734. |
| [2] | Witte F;Fischer J;Nellesen J;Crostack HA;Kaese V;Pisch A;Beckmann F;Windhagen H .In vitro and in vivo corrosion measurements of magnesium alloys[J].Biomaterials,2006(7):1013-1018. |
| [3] | Zeng R;Dietzel W;Witte F et al.[J].Advances in Engineering Materials,2008,10:3. |
| [4] | Song G;Song S .[J].Acta Physico-Chimica Sinica,2010,22:523. |
| [5] | 朱艳英,武光明,赵清.镁基生物医用材料研究进展[J].中国生物医学工程学报,2010(06):932-938. |
| [6] | Kumar S;Jamseh M;Tsn Sankara Narayanan.[J].Metals and Materials Society/AIME,2010(02):14. |
| [7] | Ma X L;Lv Y R;Gao Z X et al.[J].Current Advances in Materials and Processes,2011,147:1170. |
| [8] | Yang Y;Kim KH;Ong JL .A review on calcium phosphate coatings produced using a sputtering process-an alternative to plasma spraying.[J].Biomaterials,2005(3):327-337. |
| [9] | 王亚明,王福会,欧阳家虎,贾德昌,周玉.AZ91镁合金表面含Ti生物复合涂层结构及腐蚀学性能[J].稀有金属材料与工程,2009(z2):739-742. |
| [10] | Balani K;Anderson R;Laha T;Andara M;Tercero J;Crumpler E;Agarwal A .Plasma-sprayed carbon nanotube reinforced hydroxyapatite coatings and their interaction with human osteoblasts in vitro[J].Biomaterials,2007(26):618-624. |
| [11] | Ya-li G;Xiong D.[J].Transactions of Materials and Heat Treatment,2011(01):109. |
| [12] | Gu Y;Khor K;Cheang P .[J].Biomaterials,2003,24(09):1603. |
| [13] | Far S;Ge Q;Vedani M et al.[J].Revista Materia,2010,15(02):103. |
| [14] | Xin Y;Liu C;Zhang X et al.[J].Journal of Materials Research,2007,22(07):2004. |
| [15] | Eliezer A;Witte F .[J].Current Advances in Materials and Processes,2010,95:17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%