本文采用溶胶凝胶法制备WO3纳米粉体,再与MnCO3固相反应合成MnWO4,掺杂得到不同配比的MnWO4一Li2WO4湿敏材料,通过丝网印刷工艺制备厚膜湿敏元件.实验研究表明在适当的工艺条件下,MnWO4中掺杂30m01%Li2WO4的材料,所制备的元件具有低湿电阻小、灵敏度高、响应速度快、湿滞小的特点,这些特点为产品的实用化提供了有利条件.SEM照片和复阻抗分析.表明,该方法制备的材料具有纳米晶粒和优良的晶界微结构,是改善元件性能的重要原因.
参考文献
| [1] | 程麟,殷志峰,凌志达.Nasicon系陶瓷湿敏材料和湿度传感器的研究[J].硅酸盐通报,2007(01):29-32,149. |
| [2] | 应皆荣,张泉荣,万春荣,姜长印,何培炯.陶瓷湿敏元件的长期稳定性问题及改进措施[J].功能材料,2001(01):7-11. |
| [3] | Qu WM.;Meyer JU.;Wlodarski W. .Comparative study on micromorphology and humidity sensitive properties of thin-film and thick-film humidity sensors based on semiconducting MnWO4[J].Sensors and Actuators, B. Chemical,2000(1/3):76-82. |
| [4] | Lei Zhang;Canzhong Lu;Yuansheng Wang;Yao Cheng .Hydrothermal synthesis and characterization of MnWO4 nanoplates and their ionic conductivity[J].Materials Chemistry and Physics,2007(2/3):433-436. |
| [5] | Dellwo U.;Meyer JU.;Keller P. .FABRICATION AND ANALYSIS OF A THICK-FILM HUMIDITY SENSOR BASED ON MNWO4[J].Sensors and Actuators, A. Physical,1997(1/3):298-302. |
| [6] | 魏少红,牛晓玉,成战胜,牛新书.溶胶-凝胶法WO3纳米粉体的气敏性能研究[J].电子元件与材料,2004(10):12-13,16. |
| [7] | 黎先财,汪文娟,柯勇,杨沂凤,饶国华.H2O2氧化水热法制备超细WO3的研究[J].中国钨业,2005(03):27-30. |
| [8] | 傅刚,陈环,陈志雄,张进修.Zn2SnO4－LiZnVO4系厚膜湿敏元件的制备和性能研究[J].功能材料与器件学报,2001(01):41-44. |
| [9] | 胡素梅.SnO2-LiZnVO4系湿敏陶瓷烧结工艺与电性能关系的复阻抗分析[J].传感技术学报,2007(04):767-769. |
| [10] | Fu G.;Chen H.;Chen ZX.;Zhang JX.;Kohler H. .Humidity sensitive characteristics of Zn2SnO4-LiZnVO4 thick films prepared by the sol-gel method[J].Sensors and Actuators, B. Chemical,2002(2/3):308-312. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%