以纳米CaCO3浆料和丁苯胶乳（SBR）为原料，将两者直接混合制得了纳米CaCO3填充型粉末橡胶复合粒子。研究表明，当粉末化体系中纳米CaCO3和SBR的重量比≥1时，纳米CaCO3兼具隔离剂和凝聚剂的作用。复合粒子的粒径随着纳米CaCO3填充量的增加而减小，所制得的复合粒子的颗粒尺寸均小于200tLm，纳米CaCO3以50nm原始粒径均匀分散在复合粒子中；其成粉机理为纳米CaCO3表面的钙离子和胶乳粒子表面的负离子发生键合作用，破乳而形成粉末橡胶复合粒子。
Powdered rubber composite particle with nano-calcium carbonate filled was prpeared by simply blending nano-CaCOa slurry and styrene-butadiene latex. It was demonstrated that nano-CaCO3 could served as both separant and coagulant in the powdering system when the weight ratio of nano-CaCO3 to SBR was greater than 1. The size of the composite particle decreased with increasing nano-CaCOa loading and was always smaller than 200htm, the nano-CaCO3 dispersed uniformly with the original size of 50nm in the composite particle matrix. The powdering mechanism could be described as the demulsification due to the attractive interaction of dissolved positive ion and the anion originating from the surface of CaCOa and latex respectively.
参考文献
| [1] | 张安强,王炼石.填充型橡胶的研究进展与低碳技术[J].材料研究与应用,2010(04):743-751. |
| [2] | 林雅铃,张安强,王炼石.填充型橡胶的研究进展[J].橡胶科技市场,2008(16):18-21. |
| [3] | 关爽 .功能性纳米碳酸钙的制备及性质研究[D].长春:吉林大学,2011. |
| [4] | 阳铁健,颜鑫.纳米碳酸钙表面改性技术研究进展[J].无机盐工业,2012(02):9-12. |
| [5] | 屈国梁,陈雪梅,马新胜.纳米碳酸钙对填充型粉末丁苯橡胶硫化胶力学性能的影响[J].机械工程材料,2011(01):79-82. |
| [6] | 张琦,刘力,田明,吴友平,张立群.纳米碳酸钙/炭黑并用对丁苯橡胶性能的影响[J].特种橡胶制品,2004(06):6-8,16. |
| [7] | 孙峰,卢晓,于元章.超细碳酸钙填充粉末丁苯橡胶的制备[J].合成橡胶工业,2001(05):262-264. |
| [8] | 王炼石;吴向东;贾德民 等.超细碳酸钙填充粉末丁苯橡胶的制备方法[P].中国,CNll74210,1998—02—25. |
| [9] | 屈囡梁;陈雪梅;马新胜 .纳米CaCO3填充型粉末丁苯橡胶的制备[J].合成橡胶工业,2011,33(06):433-437. |
| [10] | 陈雪梅;马新胜;陈刚 等.一种超细轻质碳酸钙浆料及其制备方法[P].中国,1634767A,2008—07—16. |
| [11] | 黄国波,童筱莉,邬润德.超细碳酸钙/粉末丁苯橡胶的制备及在PVC中的应用[J].浙江化工,2006(09):7-9. |
| [12] | Kaj Backfolk;Serge Lagerge;Jarl B. Rosenholm .The Influence of Stabilizing Agents on the Interaction between Styrene/Butadiene Latex and Calcium Carbonate: A Calorimetric and a Dynamic Electrokinetic Study[J].Journal of Colloid and Interface Science,2002(1):8-16. |
| [13] | 黄立本.粉末橡胶[M].北京:化学工业出版社,2003:130-138. |
| [14] | 曲淑英 .丁苯胶乳在含ca2+水泥浆体中的稳定性研[J].烟台大学学报（自然科学与工程版）,1997,10(03):222-225. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%