以聚乙烯吡咯烷酮(PVP)为保护剂、聚氧乙烯脱水山梨醇单油酸酯(吐温-80)为表面活性剂、抗坏血酸为还原剂,还原AgNO3溶液制备了粒径为0.7～2.0 μm的高分散性微细球状银粉.利用X线衍射(XRD)和扫描电镜(SEM)对银粉进行表征.结果表明:PVP和吐温-80的二元分散体系产生了协同作用,通过调节其配比和用量,可以控制化学还原反应的形核和生长速率,在少量分散剂存在条件下获得分散性良好、形貌和粒径均匀、振实密度较高的银粉;当质量比m(吐温-80+ PVP)/m(AgNO3)为0.03、m(吐温-80)/m (PVP)为3.5、反应体系pH值为5、反应温度为25℃时制得的银粉分散性好,平均粒径为1.25 μm,振实密度达到4.6 g/cm3;通过同时改变还原液和银液的pH值可以有效控制银粉的粒径.
参考文献
| [1] | 郭桂全,甘卫平,罗贱,向锋,张金玲,周华,刘欢.正交设计法优化高分散超细银粉的制备工艺[J].稀有金属材料与工程,2011(10):1827-1831. |
| [2] | Mohamed M.Hilali;Kenta Nakayashiki;Chandra Khadilkar .Effect of Ag Particle Size in Thick-Film Ag Paste on the Electrical and Physical Properties of Screen Printed Contacts and Silicon Solar Cells[J].Journal of the Electrochemical Society,2006(1):A5-A11. |
| [3] | 孟淑媛,吴海斌,吴松平,唐元勋.超细银粉的制备及其导电性研究[J].电子元件与材料,2004(07):35-37,40. |
| [4] | Yiwei A;Yunxia Y;Shuanglong Y;Lihua D;Guorong C .Preparation of spherical silver particles for solar cell electronic paste with gelatin protection[J].Materials Chemistry and Physics,2007(1):158-161. |
| [5] | 王爱丽,殷恒波,任敏,姜廷顺,周全法,蒋银花,陈康敏,周卫平.不同有机官能团对室温下纳米银形貌控制合成的影响[J].贵金属,2006(02):27-34. |
| [6] | 秦智,张为军,匡加才,李文焕,杨鹏彪.丁二酸作分散剂制备球形银粉的研究[J].电子元件与材料,2010(12):11-13. |
| [7] | 甘卫平,陈迎龙,郭桂全,朱妮娜,陈志波,罗贱.以甲基纤维素作分散剂制备高分散超细银粉[J].粉末冶金材料科学与工程,2012(04):522-528. |
| [8] | 董维国,陈岁元,张继良,刘芳,刘常升,才庆魁.微细银粉的制备与应用[J].材料与冶金学报,2002(03):171-175,205. |
| [9] | 魏丽丽,徐盛明,徐刚,陈崧哲,李林艳.表面活性剂对超细银粉分散性能的影响[J].中国有色金属学报,2009(03):595-600. |
| [10] | Zhang ZT.;Hu LM.;Zhao B. .PVP PROTECTIVE MECHANISM OF ULTRAFINE SILVER POWDER SYNTHESIZED BY CHEMICAL REDUCTION PROCESSES[J].International Journal of Quantum Chemistry,1996(1):105-110. |
| [11] | Suszynska M.;Krajczyk L.;Capelletti R.;Baraldi A.;Berg KJ. .Microstructure and silver nanoparticles in ion-exchanged and deformed soda-lime silicate glasses[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2003(1/2):114-123. |
| [12] | Chou KS.;Ren CY. .Synthesis of nanosized silver particles by chemical reduction method[J].Materials Chemistry and Physics,2000(3):241-246. |
| [13] | 江建军 .化学还原法制备超细银粉[D].上海大学,2004. |
| [14] | 周宇松,曹国洲,逯庆国,侯小宝,龚朝辉,郭红燕,吴敏.高振实密度超细银粉的研制[J].兵器材料科学与工程,2007(05):22-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%