分别以聚四氢呋喃醚二醇(PTMEG)、聚氧化丙烯二醇(PPG-1000)为软段,以二苯基甲烷二异氰酸酯(MDI-50、MDI-100LL),以及扩链剂1,4-丁二醇(BDO)、三羟甲基丙烷(TMP)为硬段,采用预聚体法制备了聚氨酯弹性体。并系统研究了聚氨酯体系中各组分的种类对材料机械性能和阻尼性能的影响。
Polyurethane ( PU ) elastomers were synthesized from polyether diol, polytetramethylene-oxide glycol (PTMEG) and polypropylene glycol (PPG) as a soft segment,different isomer methylenebis (phenyl isocyanate) (MDI-50,MDI-100LL),and chain extender,tri(hydroxymethyl) propane (TMP) and 1,4-butanediol (BDO) as a hard segment by two-step bulk polymerization process. The mechanical properties and loss tangent ( tan δ) of the PU elastomers were investigated.
参考文献
| [1] | 许利莎,周海军,张晓蕾,刘德居,李彦涛,瞿雄伟.聚酯型聚氨酯阻尼材料的制备与结构性能[J].高分子材料科学与工程,2012(04):125-128. |
| [2] | 方舟,仲建峰,周萌,董擎之.聚氨酯阻尼材料改性研究综述[J].石油化工技术与经济,2012(03):54-58. |
| [3] | 顾远,罗世凯,周秋明.聚氨酯阻尼材料的研究进展[J].化学推进剂与高分子材料,2011(01):46-49,54. |
| [4] | 黄志立,张聪莉,郑水蓉,凡永利,孙曼灵,张向宇.聚氨酯阻尼材料研究进展[J].热固性树脂,2010(04):49-52. |
| [5] | 邹德荣,杨姗姗,杨丹,张宇驰,崔瑞禧.HTPB/TDI/DMTDA聚氨酯弹性体研制[J].合成材料老化与应用,2008(01):38-40. |
| [6] | 文庆珍,朱金华,王源升,姚树人.高阻尼性能聚氨酯的结构设计与研究[J].武汉理工大学学报,2005(03):9-11,18. |
| [7] | 陈浩,周海军,刘德居,李彦涛.扩链剂对PPG-1000/MDI体系聚氨酯弹性体阻尼性能的影响[J].聚氨酯工业,2012(04):9-11. |
| [8] | 文庆珍,龚沈光,朱金华,赵培仲.聚氨酯阻尼材料的结构设计及其动态力学性能的研究[J].海军工程大学学报,2006(06):40-44. |
| [9] | 刘宁,周青,刘海蓉,韩艳,夏宇正.聚氨酯弹性体结构对阻尼性能及力学性能的影响[J].合成树脂及塑料,2013(05):38-42. |
| [10] | 文庆珍,朱金华,姚树人.硬段结构对聚氨酯弹性体相容性及阻尼性能的影响[J].高分子材料科学与工程,2002(04):117-120. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%