研究了Fe-Cr-Ni-C-Si-Mo系合金的激光熔覆层经700～850℃高温处理后其微观组织的变化.采用SEM、EDS、XRD、光学显微镜、Thermo-calc热力学软件等对熔覆层的组织进行了分析.结果表明,该合金熔覆态涂层的组织主要为γ(Fe,Ni,Cr)和(Cr、Fe)7C3合金碳化物.当熔覆层的处理温度低于750℃时,其显微组织没有明显变化.经850℃的处理后,其微观组织中出现了新相(Cr、Fe)23C6,且生成的(Cr、Fe)23C6不易长大,并对其转变过程进行了研究.
参考文献
| [1] | A. Klimpel;L.A. Dobrzanski;A. Lisieciki .The study of the technology of laser and plasma surfacing of engine valves face made of X40CrSiMo10-2 steel using cobalt-based powders[J].Journal of Materials Processing Technology,2006(1/3):251-256. |
| [2] | 罗天友,宁志坚,揭晓华,蒋涛.气门锥面等离子喷焊钴基合金层的高温磨损特性研究[J].汽车工艺与材料,2006(10):5-8. |
| [3] | Q. J. Zhu;X. H. Wang;S. Y. Qu .Microstructure and wear properties of laser clad Fe based amorphous composite coatings[J].Surface Engineering,2009(3):201-205. |
| [4] | Manna I;Majumdar JD;Chandra BR;Nayak S;Dahotre NB .Laser surface cladding of Fe-B-C, Fe-B-Si and Fe-BC-Si-Al-C on plain carbon steel[J].Surface & Coatings Technology,2006(1/2):434-440. |
| [5] | W. H. Jiang;R. Kovacevic .SLURRY EROSION RESISTANCE OF LASER CLAD FE-CR-B-SI COATINGS[J].Surface Engineering,2004(6):464-468. |
| [6] | 粉末高温合金平衡相析出行为的热力学对比[J].北京科技大学学报,2005(05):571-576. |
| [7] | 周勇,郎宇平,荣凡,刘培英.Fe-17Mn-13Cr-0.3N奥氏体不锈钢的晶间腐蚀研究[J].钢铁研究,2008(01):38-43,54. |
| [8] | 赵海云;吴晓雷;陈光南 .铁基抗高温磨损激光熔覆涂层强韧设计和研究Ⅱ:Fe-Cr-C-W-Ni激光熔覆层的微观组织及性能[J].应用激光,1999,19(10):214-217. |
| [9] | 武晓雷;陈光南 .铁基合金激光熔覆组织及高温时效转变的TEM研究[J].金属热处理学报,1999,20(03):18-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%