采用液相等离子体电解渗方法,在80%甘油水溶液中实现了304不锈钢表面快速渗碳。研究施加电压和放电时间对渗碳过程的影响,分析了渗碳层的显微组织,并比较了不同工艺条件下渗碳层显微硬度分布。结果表明:经过5 min的快速放电处理,渗碳层厚度接近100μm,硬度达到880 HV。在350 V和3 min渗透条件下渗碳层质量较好。
Rapid carburization on 304 stainless steel was achieved by plasma electrolytic carburizing in 80% glycerin aqueous solution.The influence of applied voltage and discharge duration on carburizing process were investigated,and the microstructure and microhardness profiles of carburized layers under different condition were analyzed.The results show that after rapid discharge for 5 min,the depth of carburized layer is close to 100 μm and its microhardness is up to 880 HV.It is found that the carburized layer obtained under 350 V and 3 min conditions has higher performance.
参考文献
[1] | 郦振声;杨明安.现代表面工程技术[M].北京:机械工业出版社,2007:252-370. |
[2] | Nie X;Hao Q;Wei J .A novel modification technique for metal surface[J].J Wuhan U niv Technol,1996,11:28-35. |
[3] | Tarakci M;Korkmaz K;Gencer Y;Usta M .Plasma electrolytic surface carburizing and hardening of pure iron[J].Surface & Coatings Technology,2005(2/3):205-212. |
[4] | 田占军,李杰,沈德久,王玉林,刘凯.液相等离子体电解渗碳、渗氮及其碳氮共渗技术[J].电镀与涂饰,2006(02):53-56. |
[5] | 潘红梅,何翔.等离子体快速渗氮技术的实现[J].中南民族大学学报(自然科学版),2007(02):65-68. |
[6] | Nie X;Wang L;Yao ZC;Zhang L;Cheng F .Sliding wear behaviour of electrolytic plasma nitrided cast iron and steel[J].Surface & Coatings Technology,2005(5/6):1745-1750. |
[7] | Nie X.;Wilson A.;Yerokhin AL.;Leyland A.;Matthews A.;Tsotsos C. .Characteristics of a plasma electrolytic nitrocarburising treatment for stainless steels[J].Surface & Coatings Technology,2001(2/3):135-142. |
[8] | Yerokhin AL.;Tsotsos C.;Wilson AD.;Nie X.;Matthews A.;Leyland A. .Duplex surface treatments combining plasma electrolytic nitrocarburising and plasma-immersion ion-assisted deposition[J].Surface & Coatings Technology,2001(0):1129-1136. |
[9] | 薛文斌,金乾,朱庆振,吴晓玲.不锈钢在甘油体系中等离子体电解渗碳层特性研究[J].航空材料学报,2010(04):38-42. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%