Superfine alumina powder with high purity (mean particle size is less than 0. 35μm) were used as main starting material for sintering alumina ceramic. A multiple additive MgO-ZrO2 (Y2O3) was homogeneously added into the batch by the chemical coprecipitation method. Sintering of alumina bioceramic at low tempera ture (＜1600C) was achieved resulting in a dense and high strength alumina ceramic with the bending strength up to 382 MPa and an improved fracture toughness. Mechanism that the multiple additives promote the sintering of alumina ceramic is discussed on the base of XRD and SEM analysis.
参考文献
| [1] | Bo Zhanman;He Hongsheng .Study of Microcrystal Alumina Ceramic Sintered at Low Temperature[J].硅酸盐学报,1995,23(03):272. |
| [2] | W D Kingery;H K Bowen;D R Uhlmann.Introduction to Ceramics(Second Edition)[M].John Wiley &Sons,Inc,1976 |
| [3] | A M Alper;R N Mcnolly .RCDoman.Scienceof Ceramics[J].American Ceramic Society Bulletin,1964,43(09):643. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%