以Bi(NO3)3、NH4VO3为原料,NaOH为pH调节剂,采用微波水热法在180℃制备了BiVO4微球,分析了不同煅烧温度对晶型、形貌的影响,并进一步探讨了BiVO4晶型与其光催化性能的关系。采用XRD、SEM和UV-Vis吸收光谱对产品进行了分析表征,并以光催化降解亚甲基蓝为模型反应研究BiVO4的光催化性能。结果表明所制备的BiVO4微球是四方相结构,球的直径在1~3μm之间,将其在500℃煅烧后发生晶型转变,600℃煅烧可得到纯单斜相BiVO4微球,且具有良好的可见光催化活性。而且,不同晶型的BiVO4影响亚甲基蓝的降解效果。
Bismuth vanadate(BiVO4) microspheres were prepared with Bi(NO3)3 and NH4VO3 as starting materials and with NaOH to adjust pH through the microwave hydrothermal method at 180℃.The effect of different calcination temperatures on the crystalline phase and morphology was investigated,and the relationship between crystalline phase of BiVO4 and its photocatalytic performance was further studied.The as-prepared BiVO4 samples were characterized by XRD,SEM and UV-Vis.The photocatalytic activity of the BiVO4 microspheres was determined by degradation of methylene blue molecules under visible light irradiation.The results indicated that the crystalline phase of as-prepared BiVO4 microspheres was tetragonal phase,and the diameter of microspheres was 1-3μm.It is found that the phase transition had undergone after being calcined at 500℃,and monoclinic scheelite BiVO4 microspheres obtained by being calcined at 600℃ had the excellent visible-light photocatalysis.Besides,BiVO4 with different crystalline forms can affect the degradation of methylene blue molecules.
参考文献
[1] | 戈磊,张宪华.微乳液法合成新型可见光催化剂BiVO4及光催化性能研究[J].无机材料学报,2009(03):453-456. |
[2] | Gotic M;Music S;Ivanda M;Soufek M;Popovic S .Synthesis and characterisation of bismuth(III) vanadate[J].Journal of Molecular Structure,2005(0):535-540. |
[3] | Zhou L;Wang WZ;Liu SW;Zhang LS;Xu HL;Zhu W .A sonochemical route to visible-light-driven high-activity BiVO4 photocatalyst[J].Journal of molecular catalysis, A. Chemical,2006(1/2):120-124. |
[4] | Liu, W;Cao, LX;Su, G;Liu, HS;Wang, XF;Zhang, L .Ultrasound assisted synthesis of monoclinic structured spindle BiVO4 particles with hollow structure and its photocatalytic property[J].Ultrasonics sonochemistry,2010(4):669-674. |
[5] | 张爱平,张进治.水热法制备不同形貌和结构的BiVO4粉末[J].物理学报,2009(04):2336-2344. |
[6] | Tang JW;Ye J .Photocatalytic and photophysical properties of visible-light-driven photocatalyst ZnBi12O20[J].Chemical Physics Letters,2005(1/3):104-107. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%