采用共沸蒸馏法结合粉末冶金法制备了ZrO2增强钨合金(W-ZrO2).利用XRD、SEM、EDS、TEM等研究了初始溶液的pH值、还原工艺及ZrO2掺杂量对W-ZrO2复合粉末粒径及形貌的影响,观察了钨合金的显微组织及其物相组成,测定了复合钨粉的粒度、钨合金的密度、显微硬度及其磨损性能.结果表明:初始溶液的pH值对掺杂钨粉的形貌和尺寸有着显著影响,随着初始溶液的pH值增大,复合粉末颗粒尺寸逐渐增加;经750℃×2 h+850 ℃×4 h两段还原工艺后所得的复合粉末粒径细小;ZrO2对复合钨粉颗粒及钨合金晶粒细化作用明显,进而对钨合金密度及硬度产生显著影响,随着ZrO2含量的增加,钨合金密度与显微硬度降低,耐磨性呈先增加后降低趋势,其中W-3％ ZrO2钨合金的耐磨性较纯钨提高了20％～40％.
参考文献
| [1] | Zhang-Jian Zhou;Juan Du;Shu-Xiang Song.Microstructural characterization of W/Cu functionally graded materials produced by a one-step resistance sintering method[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20071/2(1/2):146-150. |
| [2] | 范景莲;刘涛;成会朝;黄伯云.钨合金在高速加载条件下的动态力学性能和失效机理[J].稀有金属材料与工程,2006(6):841-844. |
| [3] | Bjorklund KL.;Lu J.;Heszler P.;Boman M..Kinetics, thermodynamics and microstructure of tungsten rods grown by thermal laser CVD[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,20021/2(1/2):41-48. |
| [4] | 王迎春;姚志涛;程兴旺;吴复尧;王富耻.Y2O3对钨合金微观组织与性能的影响[J].北京理工大学学报,2007(9):824-827. |
| [5] | 任永国;刘自强;杨凯;周焕忠;顾幸勇.氧化锆材料种类及应用[J].中国陶瓷,2008(4):44-46. |
| [6] | 钟金豹;黄传真.不同晶型纳米氧化锆增韧氧化铝基陶瓷刀具材料研究[J].工具技术,2010(2):23-27. |
| [7] | 李嘉;尹衍升;谭训彦.ZrO2（3Y）/Fe3Al复合材料的显微结构及性能[J].无机材料学报,2004(1):189-195. |
| [8] | 卢平;沈春英;丘泰.溶胶-凝胶法制备稀土CeO2掺杂纳米钨粉的研究[J].粉末冶金技术,2008(6):455-458. |
| [9] | 林高安.钨粉形貌与粒度分布对成形性和压坯强度的影响[J].粉末冶金材料科学与工程,2009(04):260-264. |
| [10] | 陈勇;吴玉程;于福文;陈俊凌.La2O3弥散强化钨合金的组织性能研究[J].稀有金属材料与工程,2007(5):822-824. |
| [11] | 陈一胜;朱志云;陈辉煌.稀土元素对掺杂钨粉还原过程及性能的影响[J].中国钨业,2006(6):39-41. |
| [12] | 卢平;沈春英;丘泰.掺杂稀土CeO2亚微米钨粉的制备[J].粉末冶金工业,2008(2):6-8. |
| [13] | 赵中里;安林;吴大鸣;韩静涛.Zr02（3Y）／WC-20％Co金属陶瓷复合材料的耐磨性[J].材料热处理学报,2012(1):26-30. |
| [14] | 黄劲松;周继承;刘文胜;黄伯云.钨基高密度合金的烧结[J].粉末冶金材料科学与工程,2003(1):34-39. |
| [15] | 闫洪;窦明民;李和平.二氧化锆陶瓷的相变增韧机理和应用[J].陶瓷学报,2000(1):46-50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%