采用化学转化法在镁合金表面制备锡酸盐转化膜.采用硫酸铜点滴实验、电化学交流阻抗(EIS)测试和Tafel曲线、扫描电子显微镜(SEM)测试和X射线衍射分析(XRD)等方法检测膜层的性能.研究了几种有机添加剂(Tartaric acid、Citric acid、Phytic acid、EDTA、Sodium dodecyl sulfate)对膜层耐蚀性的影响,结果表明溶液中添加SDS后,转化膜的硫酸铜点滴时间由35 s提高到了86 s,明显提高转化膜的耐腐蚀性能,膜层的形貌为呈“颗粒”状紧凑的连接到一起,该膜层的主要成分为MgSn(OH)6、Mg(OH)2.
A stannate conversion coating was prepared on the AZ91D magnesium alloy surface by a chemical conversion process.The coating performances were tested by CuSO4 drip experiment,EIS,Tafel,SEM and XRD.The effects of some organic additives including tartaric acid,citric acid,phytic acid,EDTA,and sodium dodecyl sulfate on the coating corrosion resistance were studied.The results show that the drip time is increased from 35 to 86 s by adding sodium dodecyl sulfate and it could improve the corrosion resistance of the film to a large extent.The morphology of the membrane layer mainly contains MgSn(OH)6 and Mg(OH)2 which is granular-bonded.
参考文献
| [1] | 谢鲲,崔洪芝,孙金全,夏鹏成,岳丽杰,曹梅青,陈蕴博.AZ91表面熔滴涂覆Al涂层的研究[J].稀有金属材料与工程,2011(04):661-664. |
| [2] | 李新雷,郝启堂,蔡增辉,介万奇.镁合金低压铸造连续化生产技术的研究[J].稀有金属材料与工程,2011(04):718-722. |
| [3] | 李建中,田彦文,崔作兴.镁合金微弧氧化-化学镀的研究[J].稀有金属材料与工程,2007(03):528-532. |
| [4] | 张新平,熊守美,沈厚发,柳百成.镁合金表面覆盖层形成方法及相关国家标准[J].材料科学与工艺,2005(06):627-632,636. |
| [5] | 边风刚,李国禄,刘金海,刘家浚.镁合金表面处理的发展现状[J].材料保护,2002(03):1-4. |
| [6] | 郭毅,鲁彦玲,杜仕国.镁合金表面稀土转化膜研究进展[J].表面技术,2009(04):63-65. |
| [7] | 尚伟,陈白珍,石西昌,肖湘.添加剂对AZ91D镁合金微弧氧化膜的影响[J].稀有金属材料与工程,2009(02):335-338. |
| [8] | Suqiu Jia;Wenke Gao;Zhankui Zhao .Corrosion Behaviour of Mg-7.3AI Alloy in Buffered Chloride Solutions[J].Materials Science Forum,2011(TN.686):11-16. |
| [9] | Zhang WX;He JG;Jiang ZH;Jiang Q;Lian JS .Electroless Ni-P layer with a chromium-free pretreatment on AZ91D magnesium alloy[J].Surface & Coatings Technology,2007(26):4594-4600. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%