The effects of some intercritical annealing parameters including heating rate, soaking temperature, soaking time, and quench media on the microstructure and mechanical properties of cold-rolled dual phase steel were studied. The microstructure of specimens quenched after each annealing stage was analyzed using optical microscope. The tensile properties, determined for specimens submitted to complete annealing cycles, were influenced by the volume fractions of multiphases (originated from martensite, bainite, and retained austenite) , which depend on the annealing process parameters. The results obtained showed that the yield strength and the ultimate tensile strength increase with increasing the intercritical temperature and cooling rate. This can be explained by higher martensite volume ratio with the increased volume fraction of austenite formed at the higher temperatures and cooling rates.
参考文献
| [1] | Dual-Ten (Dual Phase) Steels[EB/OL].http://www.ussteel.com/corp/auto/tech/grades/advanced/dual-ten.asp,2009-11-30. |
| [2] | Speich G R.Physical Metallurgy of Dual Phase Steels Fundamentals of Dual Phase Steels[M].New York:McGraw-Hill,1981 |
| [3] | Liu D S;Militzer M;Poole W J .Microstructure Model for a Dual-Phase Steel[J].Materials Science Forum,2003,414/ 415:101. |
| [4] | M Takahashi;A. Uenishi;H. Yoshida;H. Kuriyama .Advanced High Strength Steels for Automobile Body Structures[J].Materials Science Forum,2007(5):4386-4390. |
| [5] | Erdogan Mehmet .Effect of Austenite Dispersion Phase Transformation in Dual Phase Steel[J].Scripta Materialia,2003,48(05):501. |
| [6] | Saleh M H;Priestner R .Retained Austenite in Dual Phase Silicon Steels and Its Effect on Mechanical Properties[J].Journal of Materials Processing Technology,2001,113(1/2/3):587. |
| [7] | P.Jacques .Enhancement of the Mechanical Properties of a Low-Carbon, Low-Silicon Steel by Formation of a Multiphased Microstructure Containing Retained Austenite[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1998(9):2383-2394. |
| [8] | Pereira M S;Garcia P E L;Hashimoto T M .Metallographic Procedure to Microstructural Characterization of Multiphase Steel Applied to Pipelines Industry by Optical Microscopy[J].Microscopy Microanalyses,2002,8(z2):1328. |
| [9] | Rocha R O;Melo T M F;Pereloma E V et al.Microstructural Evolution at the Initial Stages of Continuous Annealing of Cold Rolled Dual phase Steels[J].Materials Science and Engineering,2005,391A(1/2):296. |
| [10] | Bello K A;Hassan S B;Abdulwahab M et al.Effect of Fer-rite-Martensite Microstructural Evolution on Hardness and Impact Toughness Behavior of High Martensite Dual Phase Steel[J].Australian Journal of Basic and Applied Sciences,2007,1(04):407. |
| [11] | Samuel F H;Hussein A A .Microstructure and Mechanical Properties of a Quenched and Tempered Cr-V Dual-Phase Steel[J].Transactions of the Iron and Steel Institute of Japan,1983,23(03):213. |
| [12] | K.Dehghani;J.J. Jonas .Dynamic Bake Hardening of Interstitial-Free Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(5):1375-1384. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%