采用非均相形核法,以HCl为酸化剂在TiH_2颗粒发泡剂表面合成了SiO_2包覆层,并进行释氢试验.采用扫描电子显微镜(SEM)和能谱(EDS)对包覆层结构进行了分析,探讨了包覆层延缓释放氢气的机理.结果表明,pH值对发泡剂表面的成膜过程影响较大,当溶液pH值为9.5时SiO_2在TiH_2颗粒表面形成致密的包覆层;制得的发泡剂有效延迟释氢时间可达120s.
The TiH_2 particles coated with SiO_2 are prepared using heterogeneous nucleation method with acidification HCl.The structure and the forming mechanisms of the layer are researched.At the end,the hyarogen released experiments are also tested.The result shows that the uniform and compact SiO_2 film can be obtained at the pH=9.5,which can delay the hydrogen releasing time up to 120s.
参考文献
| [1] | Banhart J .Manufacture,characterization and application of cellular metals and metal foams[J].Progress in Materials Science,2001,46:559. |
| [2] | 陈文革,张强.泡沫金属的特点、应用、制备与发展[J].粉末冶金工业,2005(02):37-42. |
| [3] | 陈思杰,米国发.泡沫铝的制备工艺、组织性能及应用前景[J].热加工工艺,2005(05):54-57. |
| [4] | 姜斌,赵乃勤.泡沫铝的制备方法及应用进展[J].金属热处理,2005(06):36-40. |
| [5] | 梁永仁,杨志懋,丁秉钧.金属多孔材料应用及制备的研究进展[J].稀有金属材料与工程,2006(z2):30-34. |
| [6] | Prakash O;Emburyj D;Sang H.Synthesis/processing of light weight metallic materials Ⅱ[J].Miner Metals Mater Soc,1997(03):122. |
| [7] | 韩福生;朱震刚;刘长松 .孔径可调泡沫铝的制备方法[P].中国,96117125.1,1996-10-10. |
| [8] | 方吉祥,赵康,谷臣清.化学法制备Al2O3包覆TiH2颗粒发泡剂[J].中国有色金属学报,2002(06):1205-1209. |
| [9] | 王怡红;赵军;宋苇.TiH_2的SiO_2凝胶包裹对其释氢的影响[J].东南大学学报(自然科学版),1999(11):145. |
| [10] | 陈永楠,梁戈,张从容,赵康.SiO2/Al2O3复合包覆TiH2颗粒发泡剂的制备[J].材料工程,2006(02):23-25,55. |
| [11] | 张从容 .泡沫铝用新型复合包覆发泡剂的制备研究[D].西安:西安理工大学,2004. |
| [12] | 饶东升.硅酸盐物理化学[M].北京:冶金工业出版社,1991:222. |
| [13] | 崔爱莉,王亭杰,金涌.SiO2和Al2O3在TiO2表面的成核包覆与成膜包覆[J].化工冶金,1999(02):178-181. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%