Laser Shock Processing of an Austenitic Stainless Steel and a Nickel-base Superalloy

材料科学技术（英文）, 2003, 19(5): 402-404.

^1, , ^2, , ^3,

1.Laboratory of Laser Materials Processing and Surface Engineering, School of Materials Science and Engineering, Beihang University formerly Beijing University of Aeronautics and Astronautics, Beijing 100083, China

2.Laboratory of Laser Materials Processing and Surface Engineering, School of Materials Science and Engineering, Beihang University formerly Beijing University of Aeronautics and Astronautics, Beijing 100083, China

3.Laboratory of Laser Materials Processing and Surface Engineering, School of Materials Science and Engineering, Beihang University formerly Beijing University of Aeronautics and Astronautics, Beijing 100083, China

基金项目: This research was supported by the Aviation Fund of China

Laser Shock Processing of an Austenitic Stainless Steel and a Nickel-base Superalloy

Keywords： Laser shock processing

An austenitic stainless steel 1Cr18Ni9Ti and a solid solution-strengthened Ni-base superalloy GH30 were shock processed usinga Q-switched pulsed Nd-glass laser. Microstructure, hardness and residual stress of the laser shock processed surface wereinvestigated as functions of laser processing parameters. Results show that high density of dislocations and fine deformationtwins are produced in the laser shock processed surface layers in both the austenitic stainless steel and the nickel-base superalloy.Extensive strain-induced martensite was also observed in the laser shock processed zone of the austenitic steel. The hardnessof the laser shock processed surface was significantly enhanced and compressive stress as high as 400 MPa was produced inthe laser shock processed surface.

参考文献

[1]	K Eisner;A Lang;K Schutte;H W Bergmann .[J].SPIE,1996,2789:274.
[2]	P Peyre;R Fabbro;P Merrien;H P Lienrade .[J].Materials Science and Engineering,1996,A210:102.
[3]	N C Anderholm .[J].Applied Physics Letters,1970,16:113.
[4]	B P Fairand;B A Wilcox;W J Gallagher;D W Williams .[J].Journal of Applied Physics,1972,43:3893.
[5]	B P Fairand;A H Claner .[J].Journal of Applied Physics,1979,50:1497.
[6]	J A Vaccari.[J].American Mechanist,1992(07):62.
[7]	P Peyer;R Fabbro;L Berthe;C Dubouchet.[J].Journal of Laser Applications,1996(08):135.
[8]	C.B.Dane;L.A.Hackel .Shot peening with lasers[J].Advanced Materials & Processes,1998(5):37-38.
[9]	G Banas;H E Elsayed-Ali;F V Lawrence;J M Rigsbee .[J].Journal of Applied Physics,1990,67:2380.
[10]	J.P. CHU;J.M. RIGSBEE;G. BANAS .Effects of Laser-Shock Processing on the Microstructure and Surface Mechanical Properties of Hadfield Manganese Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1995(6):1507-1517.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Laser Shock Processing of an Austenitic Stainless Steel and a Nickel-base Superalloy

参考文献