采用传统固相法，制备了Dy1-xSrxFeO3（x=0、0．1、0．2、0．3、0．4）粉体，研究了其微波电磁性能。利用X射线衍射技术研究了其结构和相组成。利用扫描电镜观察粉体颗粒微观形貌。利用网络分析仪测试了其2-18GHz的电磁参数，并通过软件对其微波吸收性能进行了模拟，利用紫外-可见-红外分光光度计测量了其在930-1250nm波长区间的反射率。结果表明粉体为钙钛矿结构；当x=0．3，涂层厚度d=2．8ram时，在11GHz处吸收出现峰值，约为-20dB，2-18GHz范围内吸收〉-10dB的频宽约为2．9GHz；当x=0．3时，粉末压片在950-1200urn波长区间的红外吸收性能最好，其反射率约为0．05％。
In this paper, Dy1-xSrxFeO3（x = 0, 0.1, 0.2, 0.3, 0.4） were prepared by the conventional souo- state reaction and the microwave magnetic performance were also studied. The phase structure, morphology and particle size of Dy1-xSrxFeO3 powders were characterized by X-ray diffraction and scanning electron microscope. The electromagnetic properties were measured by network analyzer, and then the microwave absorption were calculated using YR computer reflection simulating software. The reflection spectra were measured by spectro- photometer（930-1250nm）. The results show that the powders are perovskite structure, and the reflection loss of single-layer coating （the thickness is 2.8mm） reaches the peak value about -20dB when x=0.3, and the bandwidth （RL≥-10dB） reaches 2. 9GHz, and when x=0. 3, the reflectivity （950-1200nm） reaches to 0. 05%.
参考文献
| [1] | Satoshi S;Kazuaki H;Toshio K et al.[J].J MagnMagn Mater,2005,290-291:1188-1191. |
| [2] | 邹田春,赵乃勤,师春生,李家俊.吸波材料吸波性能的计算及其优化设计[J].功能材料,2005(07):988-991,995. |
| [3] | 邵蔚,赵乃勤,师春生,李家俊.吸波材料用吸收剂的研究及应用现状[J].兵器材料科学与工程,2003(04):65-68. |
| [4] | Wang L X;Song J;Zhang Q F et al.[J].J AlloysCompd,2000,481:863-866. |
| [5] | 胡国光,尹萍,吕庆荣.LaxSr1-xMnO3氧化物的导电和吸收特性[J].中国稀土学报,2002(02):179-181. |
| [6] | 仲崇贵,蒋青,方靖淮,葛存旺.单相ABO3型多铁材料的磁电耦合及磁电性质研究[J].物理学报,2009(05):3491-3496. |
| [7] | 刘建,云国宏,杨智慧,吴江波,张飞,王耀强,徐文清,李晓平,苏美琳,杨丹.La2/3Sr1/3MnO3掺杂RE（RE=Pr、Eu、Y、Tb）的结构、红外及磁学性质[J].功能材料,2007(09):1443-1446. |
| [8] | 李姝丹;井立强;付薇 等.[J].哈尔滨工业大学学报,2007,21(10):1465-1470. |
| [9] | 戴道生;熊光成;吴思诚 .[J].物理学进展,1997,17(02):201-222. |
| [10] | Yoshiteru I;Masami M;Yuuki H et al.[J].Sens Ac-tuators B,2007,122:315-320. |
| [11] | 张晖,刘拥军,潘丽华,张瑜.Co掺杂BiFeO3的第一性原理研究[J].物理学报,2009(10):7141-7146. |
| [12] | 汪正红,冯绍杰,杨萍华.Sr2Fe1-xMgxMoO6复合氧化物的甲烷催化燃烧性能研究[J].中国科学技术大学学报,2010(04):358-362. |
| [13] | Zhang Q T;Wang T W;Meng X F et al.[J].Journal of Rare Earths,2005,23:295-298. |
| [14] | Chern G.;Tai MF.;Hsung KS.;Hsieh WK. .High dielectric permittivity and hole-doping effect in La1-xSrxFeO3[J].Physical Review.B.Condensed Matter,1998(3):1252-1260. |
| [15] | 张栋杰;都有为 .[J].压电与声光,2009,24(05):415-417. |
| [16] | 刘向春,高峰,邓军平,田长生.ABO3型钛铁矿结构化合物的容差因子[J].无机材料学报,2008(05):881-885. |
| [17] | John B;Goodenough .[J].Physical Review,1955,100:564-573. |
| [18] | 寇昕莉;秦勇;何海英 等.[J].材料科学与工艺,2009,12(02):140-143. |
| [19] | 刘顺华;刘军民;董星龙.电磁波屏蔽及吸波材料[M].北京:化学工业出版社,2006:207. |
| [20] | 黄昆;韩汝琦.固体物理学[M].北京:高等教育出版社,1988:441. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%