采用硬度测试、室温拉伸性能测试、光学显微镜、扫描电镜及透射电镜等方法研究了锌镁元素含量对Al-3Zn-4.5Mg-1Cu 、A1-4Zn-3.5 Mg-1Cu和Al-4.5Zn-3.5Mg-1Cu 3种高强铝合金挤压棒材的显微组织、时效硬化行为和力学性能的影响.结果表明,Al-4.5Zn-3.5Mg-1Cu合金的时效硬化效果最显著,经120℃×24 h时效后维氏硬度达183 HV3,抗拉强度达617 MPa,屈服强度为590 MPa,伸长率为10.2％.Zn元素含量或Zn/Mg比值升高增加了时效时沉淀强化相的密度,减小了其尺寸,从而提高了强化效果.
参考文献
| [1] | 方华婵;陈康华;巢宏;陈祥;叶登峰.Al-Zn-Mg-Cu系超强铝合金的研究现状与展望[J].粉末冶金材料科学与工程,2009(6):351-358. |
| [2] | Liu, S. D.;Chen, B.;Li, C. B.;Dai, Y.;Deng, Y. L.;Zhang, X. M..Mechanism of low exfoliation corrosion resistance due to slow quenching in high strength aluminium alloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2015Feb.(Feb.):203-212. |
| [3] | T. Marlaud;B. Malki;C. Henon;A. Deschamps;B. Baroux.Relationship between alloy composition, microstructure and exfoliation corrosion in Al-Zn-Mg-Cu alloys[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,201110(10):3139-3149. |
| [4] | 陈送义;陈康华;贾乐;彭国胜.热变形条件对7085铝合金晶粒结构和性能的影响[J].中国有色金属学报（英文版）,2013(2):329-334. |
| [5] | 戴晓元;李妮;熊亮;石志豪.Al-Zn-Mg-Cu-Zr-0.2Sc合金的淬火敏感性[J].材料热处理学报,2014(12):62-66. |
| [6] | 刘晓涛;崔建忠.Al-Zn-Mg-Cu系超高强铝合金的研究进展[J].材料导报,2005(3):47-51. |
| [7] | 欧阳惠 .Zn/Mg比对Al-Zn-Mg-Cu合金淬火敏感性的影响[D].中南大学,2013. |
| [8] | 刘胜胆;李承波;欧阳惠;邓运来;张新明;刘星兴.超高强7000系铝合金的淬火敏感性[J].中国有色金属学报,2013(4):927-938. |
| [9] | 张新明;张小艳;刘胜胆;刘瑛.固溶后降温预析出对7A55铝合金力学及腐蚀性能的影响[J].中南大学学报（自然科学版）,2007(5):789-794. |
| [10] | 唐建国;陈慧;张新明;刘胜胆;刘文军;欧阳惠;李红萍.淬火析出对Al-Zn-Mg-Cu合金时效行为的影响[J].中国有色金属学报（英文版）,2012(6):1255-1263. |
| [11] | Zhang, X.;Liu, W.;Liu, S.;Zhou, M..Effect of processing parameters on quench sensitivity of an AA7050 sheet[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20113(3):795-802. |
| [12] | S.K.Maloney;K.Hono.The chemistry of precipitates in an aged Al-2.1Zn- 1.7Mg at. percent alloy[J].Scripta materialia,199910(10):1031-1038. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%