利用等离子体对废橡胶胶粉(SRP)进行了表面处理,并将其与聚氯乙烯(PVC)进行共混,研究了等离子体处理前后胶粉/PVC复合材料的结构和性能.结果表明,胶粉等离子体改性后,不仅提高了胶粉与PVC之间的粘接强度,而且提高了PVC/SRP复合材料的力学性能.采用氧等离子处理2 min后,PVC/SRP复合材料具有较好的力学性能.扫描电镜观察(SEM)表明,未处理胶粉/PVC复合材料的冲击断裂形貌表现为胶粉的脱落;等离子体处理后胶粉/PVC复合材料冲击断裂形貌则表现为胶粉的本体破坏.
参考文献
[1] | Michel D J R et al.[J].Plastics Rubber and Composites Processing and Applications,1991,15:87-93. |
[2] | Ryu S H .[J].Journal of Applied Polymer Science,2000,77:2595-2602. |
[3] | Rajalingam P et al.[J].Rubber Chemistry and Technology,1993,66:664-677. |
[4] | Makarow V M.[M].New York:Ellis Horwood,1991:177-194. |
[5] | Dessouki A M et al.[J].Polymer-Plastics Technology and Engineering,1997,36:241-256. |
[6] | Leyden J J .[J].Rubber World,1991,203:28. |
[7] | Isayev AI.;Tukachinsky A.;Chen J. .NOVEL ULTRASONIC TECHNOLOGY FOR DEVULCANIZATION OF WASTE RUBBERS[J].Rubber Chemistry and Technology,1995(2):267-280. |
[8] | Johnston ST.;Vonmeerwall E.;Kim SH.;Levin VY.;Isayev AI.;Massey J. .ULTRASOUND DEVULCANIZATION OF SBR - MOLECULAR MOBILITY OF GEL AND SOL[J].Rubber Chemistry and Technology,1997(2):183-193. |
[9] | Fix S R .[J].Elastomerics,1980,112:38-40. |
[10] | 周文 等.[J].合成橡胶工业,1995,18:374-378. |
[11] | 樊世民,盖国胜,苗赫濯.碳酸钙的等离子体表面改性[J].表面技术,2002(02):5-8. |
[12] | 蔡汉海,卢光,李思东,谢健.低温等离子体技术在橡胶制品中的应用[J].特种橡胶制品,2001(05):40-42,51. |
[13] | Kaynak C et al.[J].Polymer,2001,42:4393-4399. |
[14] | Choudhury N R et al.[J].Journal of Applied Polymer Science,1989,38:1091-1109. |
[15] | Kano Y S et al.[J].Polymer Networks and Blends,1996,6:105-111. |
[16] | Schonhorn H et al.[J].Polymer Engineering and Science,1977,17:440-449. |
[17] | Hall J R et al.[J].Journal of Colloid and Interface Science,1974,47:472-484. |
[18] | Kim C Y et al.[J].Journal of Applied Polymer Science,1971,15:1365-1375. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%