以整体毡为增强体,丙烯和糠酮树脂为前驱体,采用分区CVI法和树脂浸渍/固化、炭化相结合的工艺制备了厚壁C/C复合材料,用CT机和偏光显微镜观察了材料的微观结构,并进行了热力学性能测试,结果与热梯度CVI法进行了对比.研究结果表明:分区CVI法制备的热解碳为光滑层结构,整体密度均匀,与热梯度CVI工艺相比,总CVI增密效率提高了近一半,特别是沉积后期,表现出明显的优势.同时,轴向压缩强度提高了28.5%;径向压缩强度提高了33.6%.线胀系数相当.通过研究认为,分区CVI法能很好的提高材料的增密效率和增密均匀性,降低成本,且材料最终具有优异的热力学性能.

参考文献

[1] Torsten Windhorst;Gordon Blount .Carbon-carbon composites:a summary of recent developments and applications[J].Materials & Design,1997,18(01):11-15.
[2] M. Lacoste;A. Lacombe;P. Joyez .Carbon/Carbon extendible nozzles[J].Acta astronautica,2002(6):357-367.
[3] Baker C F.A high temperature,light weight,nozzle material[A].,1994:27-29.
[4] 李贺军.炭/炭复合材料[J].新型炭材料,2001(02):79-80.
[5] Zhang W G;Huttinger K J .Influence of pressure temperature and surface area/volme ratio on the texture of pyrolytic carbon deposition from methane[J].Carbon,2003,41(12):749-758.
[6] Besmann T M;Sheldon B W .Vapor-phase fabrication and properties of continuous-filament ceramic composites[J].Science,19991,25(06):1104.
[7] 顾正彬,李贺军,李克智,李爱军.碳/碳复合材料等温化学气相渗透工艺模糊系统建模[J].硅酸盐学报,2003(07):629-634.
[8] Glasier G F;Pacey P D .Fonnation of pyrolytic carbon during the pyrolysis of ethane at high conversions[J].Carbon,2001,39:15-23.
[9] John D B;Dan D.Carbon-carbon materials and composites[M].Noyes Publications,1993
[10] 罗瑞盈 .碳/碳材料快速CVD工艺结构性能及应用研究[D].西安:西北工业大学,1995.
[11] 邓景屹,刘文川,杜海峰,成会明,李依依.热梯度法化学气相渗温度控制[J].炭素技术,1999(06):22-24.
[12] Lackey W J .Review,Status and facture of the chemical vapor infiltration process for fabrication of fiber-reinforced ceramic composites[J].Ceramic Engineering and Science Proceedings,1989,10(7/8):577-584.
[13] Pierson H O;Lieberman M L .The chemical vapor deposition of carbon on carbon fibers[J].Carbon,1975,13(03):159-166.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%