用Gleeble1500D模拟试验机在变形温度为950～1 200℃、应变速率为0.01～8s-1、最大变形程度为60%的条件下,对硅钢50A1300做单道次压缩试验,首先分析了不同参数对流变应力的影响,然后用回归法确定了应力模型中的变形激活能及材料常数,得到硅钢50A1300在峰值应力条件和稳态应力条件下的变形激活能分别为270.360和91.557kJ/mol,同时得到了流变峰值应力模型,模型的相关系数为0.997。最后通过作lnθ-ε图的方法找到了硅钢50A1300发生动态再结晶的临界应变量,并回归得到峰值应变量、临界应变量与参数Z/C的关系式。
To analyze the effects of different parameters on the flow stress and critical strain of the dynamic recrystallization,single-pass compression experiments were carried out with silicon steel 50A1300 specimens using a Gleeble1500D thermal simulator at a temperature range of 950-1 200 ℃ and strain rate range of 0.01-8 s-1 under the condition of maximum deformation of 60%.The average deformation activation energy is respectively 270.360 and 91.557 kJ/mol under the peak stress and steady-state stress conditions with using the regression method.Finally,the rheological peak stress model is got.The related coefficient is 0.997.The critical strain for dynamic recrystallization is found by plotting lnθ-ε,and at the same time,the relation between peak strain and the critical strain and parameters Z/C is got.
参考文献
| [1] | 徐有容;侯大华;王德英 等.10Ti钢高温变形流变应力模型及晶粒大小变化[J].钢铁,1995,30(03):33. |
| [2] | McQueen H J;Yue S;Ryan N D .Hot Working Characteristics of Steels in Austenitics State[J].Journal of Materials Processing Technology,1995,53(1/2):293. |
| [3] | 周纪华;管克智.金属塑性变形阻力[M].北京:机械工业出版社,1989 |
| [4] | 王宝景 .340MPa高强IF钢冷轧薄板罩式退火工艺研究[D].北京科技大学,2004. |
| [5] | 柳建韬 .工模钢热变形行为研究[D].上海交通大学,1998. |
| [6] | 梁桂平,白星,李落星,刘波,刘扬胜.AM80-xSr-yCa镁合金高温压缩变形行为[J].塑性工程学报,2010(01):98-103. |
| [7] | WU Lai-zhi,LI Xue-song,CHEN Jun,ZHANG Hong-bing,CUI Zhen-shan.Predicting Critical Conditions and Stress-Strain Curves for Dynamic Recrystallization in SPHC Steel[J].钢铁研究学报（英文版）,2010(07):51-57. |
| [8] | 曹金荣,刘正东,程世长,杨钢,谢建新.应变速率和变形温度对T122耐热钢流变应力和临界动态再结晶行为的影响[J].金属学报,2007(01):35-40. |
| [9] | 宋维锡.金属学[M].北京:冶金工业出版社,2005:186. |
| [10] | Davenport S B;Silk N J;Sellars C M .Development of Constitutive Equations for Modeling of Hot Rolling[J].Mater Sci Techno 1,2000,16:539. |
| [11] | 吴瑞恒 .结构钢热变形行为及其铁素体析出动力学数学模型[D].上海:上海交通大学,2002. |
| [12] | Medina S F;Hernandez C A .General Expression of the Ze ner-Hollomon Parameter as a Function of the Chemical Corn position of Low Alloy and Microalloyed Steels[J].Aeta Ma ter,1996,44(01):137. |
| [13] | Zahiri S D;Davies C H G;Hodgson P D.A Mechanical Approach to Quantify Dynamic Recrystallization in Polycrystal- line Metals[J].Scripta Materialia,2005(52):299. |
| [14] | Poliak E I;Jonas J J .Ctitical Strain for Dynamic Recrystallization in Variable Strain Rate Hot Deformation[J].ISIJ International,2003,43(05):684. |
| [15] | NAJAFIZADEH Abbas;Jonas J J .Prediction the Critical Stress for Initiation of Dynamic Recrystallization[J].ISIJ International,2006,46(11):1679. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%