利用加热炉模拟、动态再结晶以及热模拟等试验方法以及扫描电镜、金相显微镜等分析观察手段对无取向硅钢边裂的成因进行了探讨.结果表明,长时间加热使得板坯边部晶粒异常长大,晶界氧化并脱碳,轧制过程中边部温度过低,动态再结晶过程变弱,使得板坯边部延伸性能变差,是导致硅钢边裂的主要原因.建议通过适当降低铸坯加热温度、缩短保温时间、提高终轧温度来改善硅钢边裂缺陷.
参考文献
| [1] | Pierre Brissonneau .Non-oriented electrical sheets[J].Journal of Magnetism and Magnetic Materials,1984,41(1-3):38-46. |
| [2] | 石虎珍 .薄板坯连铸连轧无取向硅钢的裂纹缺陷分析[D].东北大学,2008. |
| [3] | 毛一标,樊立峰,余红春,周滨新,孟静,高海花.无取向硅钢边部缺陷的分析与解决[J].上海金属,2012(02):57-59. |
| [4] | Byoungchul Hwang;Han Sang Lee;Yang Gon Kim;Sunghak Lee .Analysis and prevention of side cracking phenomenon occurring during hot rolling of thick low-carbon steel plates[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):177-187. |
| [5] | Gareia-Sanchez E O;Trevino-Luna E A;Salinas-Rodriguez A et al.High temperature fracture mechanisms on non-oriented electrical steels[J].Recista De Metalurgia,2007,43(04):266-271. |
| [6] | 叶凌英,张新明,刘颖维,唐建国.温度对01420铝锂合金轧制开裂及晶粒细化的影响[J].稀有金属材料与工程,2008(08):1431-1435. |
| [7] | Yu Jin Jang;Sang Woo Kin .An estimation of a billet temperature during reheating furnace operation[J].International Journal of Control,Automation,and Systems,2007,5(01):43-50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%