采用改进的工艺路线制备了化学计量比的Pb(Zn1/3Nb2/3)O3-PbTiO3-BaTiO3陶瓷,二氧化钛和碳酸钡不经过预烧,与预反应粉体混合球磨,成型后直接烧结,在1100℃和1120℃分别保温1 h,2 h,4 h获得了100%钙钛矿结构的PZN-PT-BT陶瓷,最大密度7.418 g/cm3,最大介电常数7672.
Stoichiometric Pb(Zn1/3Nb2/3)O3-PbTiO3-BaTiO3(PZN-PT-BT) perovskite ceramics prepared by modified processing route were investigated. Without calcination of TiO2 and BaCO3, a mixture of pre-reaction powders (PbO+ZnNb2O6) and TiO2and BaCO3 was pressed and sintered directly. Stoichiometric PZN-PT-BT ceramics sintered at 1100℃ and 1120℃ for 1, 2 and 4 h, respectively, with 100% perovskite phase were obtained. PZN-PT-BT ceramics with density 7.418 g/cm3 (92.6% of theoretical density 8.01 g/cm3) and dielectric constant Kmax 7672 at 1 kHz were prepared. As far as energy-saving and time-saving of processing are concerned, it is a simplified and effective route to prepare PZN-PT-BT ceramics.
参考文献
| [1] | Service R E .[J].Science,1997,275:1878. |
| [2] | Yamsshita Y;Harada K;Saitoh S .[J].Ferroelectrics,1998,219:29. |
| [3] | Cross L E .[J].Japanese Journal of Applied Physics,1995,34:2525. |
| [4] | Kanagae T;Sakta K;Takenaka T .[J].Japanese Journal of Applied Physics,1991,9B:2232. |
| [5] | Shrout T R;Halliyal A .[J].American Ceramic Society Bulletin,1987,64(04):704. |
| [6] | Swartz S L;Shrout T R .[J].Materials Research Bulletin,1983,18:663. |
| [7] | Lejeune M;Boilot J P .[J].Ceramics International,1983,9(04):119. |
| [8] | Guha J P .[J].Journal of Materials Science,1999,34:4985. |
| [9] | Lucas P;Petuskey W T .[J].Journal of the American Ceramic Society,2001,84(09):2150. |
| [10] | Swartz S L;Shrout T R .[J].Materials Research Bulletin,1982,17:1245. |
| [11] | Halliyal A .[J].American Ceramic Society Bulletin,1987,66(04):671. |
| [12] | Ravidranathan P;Komarneni S .[J].Journal of the American Ceramic Society,1991,74(12):2996. |
| [13] | Fujin T;Tanaka A;Takenaka T .[J].Japanese Journal of Applied Physics,1999,30:477. |
| [14] | Wang J;Wan D et al.[J].Journal of the American Ceramic Society,2001,82(02):2150. |
| [15] | Xia F;Wang X;Yao X .[J].Ferroelectrics,1998,215:181. |
| [16] | Halliyal A;Safari A .[J].Ferroelectrics,1994,158:295. |
| [17] | Liou Y C;Tseng K H .[J].Materials Research Bulletin,2003,38:1351. |
| [18] | Liou Y C .[J].Materials Letters,2004,58:944. |
| [19] | Wang X;Chen H .[J].Journal of Applied Physics,2002,91(09):5979. |
| [20] | Xia F.;Wang XL.;Yao X. .Effects of thermal annealing on the dielectric and piezoelectric properties of PZN-PT-BT ceramics[J].Journal of Materials Science Letters,1998(10):861-863. |
| [21] | Wang X .[J].Journal of Materials Science,1999,34:6027. |
| [22] | Pei Z;Che J .[J].Nature Science Advance,2003,4(01):77. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%