制备了壳聚糖接枝丙烯酸负载纳米钯催化剂并对其催化氢化性能进行了研究。首先对分子量为30万的商品壳聚糖进行降解,得到了黏均分子量为10万的壳聚糖,用后者制备壳聚糖接枝丙烯酸共聚物并负载氯化钯,最后通过电纺丝技术得到了纳米纤维状催化剂。对制备的催化剂进行了透射电镜（TEM）,X射线光电子能谱（XPS）和红外光谱（IR）的表征。结果表明,纳米纤维的尺寸在70 nm～200 nm之间,钯颗粒在10 nm～40 nm之间,并且钯颗粒在纳米纤维上均匀分散。催化剂氢化α-辛烯,结果显示,α-辛烯的转化率为99%;该催化剂在Ni2＋存在下催化α-辛烯反应,生成辛烷的产率为65%。
Chitosan grafting acrylic copolymer（CTS-g-AA） supported nano palladium catalyst was obtained and its hydrogenation properties were studied.Firstly,chitosan was degraded,and the degraded chitosan with the viscosity average molecular weight of 1×105 was obtained via a degradation of chitosan with a molecular weight of 3×105;Then chitosan grafting acrylic copolymer（CTS-g-AA） was synthesized and palladium was supported on this CTS-g-AA,formation of nano fibrous catalyst via electrospinning technique.The title catalysts were characterized by transmission electron microscope（TEM）,X-ray photoelectron specroscopy（XPS） and infrared spectrum（IR）.The results show that the diameter of nanofiber is about 70 nm～200 nm,the size of metal particles range of 10 nm～40 nm,and palladium particles disperse on nanofibers homogeneously.The catalyst was applied to catalyze α-octene hydrogenation.The results showed that the conversion of α-octene is 99%,and the yield of octane is 65% with the help of a Ni2＋ compound.
参考文献
| [1] | Liu YF.;Huang AM.;Chen J.;Chen L.;Hua JD. .Hydrogenation catalysis of nanosized palladium supported by polymer/silica disupporter. II. Effects of the characteristics of the catalyst on hydrogenation[J].Journal of Applied Polymer Science,2003(13):3661-3665. |
| [2] | Jin WJ;Lee HK;Jeong EH;Park WH;Youk JH .Preparation of polymer nanofibers containing silver nanoparticles by using poly (N-vinylpyrrolidone)[J].Macromolecular rapid communications: Publishing the newsletters of the European Polymer Federation,2005(24):1903-1907. |
| [3] | 于建香,刘太奇.PVP负载钯纳米丝状催化剂的制备及催化加氢性能[J].高分子材料科学与工程,2008(12):191-194. |
| [4] | Jianxiang Yu;Taiqi Liu .Preparation of a Fibrous Catalyst Containing Palladium Nanoparticles and Its Application in Hydrogenation of Olefins[J].Polymer Composites,2008(12):1346-1349. |
| [5] | 王岚,刘一真,刘蒲,王向宇.壳聚糖钯配位络合物的合成、表征及其催化性能研究[J].离子交换与吸附,2004(06):501-507. |
| [6] | Supeeporn Koombhongse;Wenxia Liu;Darrell H. Reneker .Flat Polymer Ribbons and Other Shapes by Electrospinning[J].Journal of Polymer Science, Part B. Polymer Physics,2001(21):2598-2606. |
| [7] | Vaibhav B.Valodkar;Gopal L.Tembe;Marayil Ravindranathan;R.N.Ram;H.S.Rama .A study of synthesis, characterization and catalytic hydrogenation by polymer anchored Pd(II)-amino acid complexes[J].Journal of molecular catalysis, A. Chemical,2003(1/2):47-64. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%