对比研究了由液体橡胶在环氧树脂中原位形成的亚微米橡胶/环氧复合材料和在环氧树脂中直接添加纳米橡胶颗粒形成的纳米橡胶/环氧复合材料的性能.研究表明:未固化混合物的黏度随着纳米橡胶相的加入逐渐增加,但随着亚微米橡胶相含量的增加而降低;橡胶/环氧复合材料的玻璃化转变温度随着纳米橡胶颗粒的加入逐渐增加,但随着亚微米橡胶相含量的增加而降低;两种橡胶相的添加均使复合材料的弹性模量降低,断裂延伸率增加;在较低含量时,纳米橡胶颗粒可以提高环氧的拉伸强度;两种橡胶填充的橡胶/环氧复合材料均显示出明显的增韧效果.微观形貌分析表明,两种橡胶均可以在应力作用下脱粘并促进裂纹尖端的塑性变形.
参考文献
| [1] | Raju T,Ding Y M,He Y L,et al.Miscibility,morphology,thermal,and mechanical properties of a DGEBA based epoxy resin toughened with a liquid rubber[J].Polymer,2008,49(1):278-294. |
| [2] | Chikhi N,Fellahi S,Bakar M.Modification of epoxy resin using reactive liquid (ATBN) rubber[J].European Polymer Journal,2002,38(2):251-264. |
| [3] | Ratna D,Banthia A K,Deb P C.Toughening of epoxy resin using acrylate-based liquid rubbers[J].Journal of Applied Polymer Science,2000,78(4):716-723. |
| [4] | Huang F,Liu Y Q,Zhang X H,et al.Effect of elastomerie nanoparticles on toughness and heat resistance of epoxy resins[J].Macromolecular Rapid Communications,2002,23(13):786-790. |
| [5] | Ma H Y,Wei G S,Liu Y Q,et al.Effect of elastomeric nanoparticles on properties of phenolic resin[J].Polymer,2005,46(23):10568-10573. |
| [6] | MaJ,MoMS,Du X H,et al.Study of epoxy toughened by in situ formed rubber nanoparticles[J].Journal of Applied Polymer Science,2008,110(1):304-312. |
| [7] | Le Q H,Kuan H C,Dai J B,et al.Structure-property relations of 55 nm particle-toughened epoxy[J].Polymer,2010,51(21):4867-4879. |
| [8] | Qi G C,Zhang X H,Li B H,et al.The study of rubbermodified plastics with higher heat resistance and higher toughness and its application[J].Polymer Chemistry,2011,2(6):1271-1274. |
| [9] | American Society for Testing Materials.ASTM D638 Standard test method for tensile properties of plastics[J].Pennsylvania United States:ASTM International,2003. |
| [10] | American Society for Testing Materials.ASTM D5045 Standard test method for plane-Strain fracture toughness and strain energy release rate of plastic materials[S].Pennsylvania,United States:ASTM International,1999. |
| [11] | Zhang H,Zhang H,Tang L C,et al.Comparative study on the optical,surface mechanical and wear resistant properties of transparent coatings filled with pyrogenic and colloidal silica nanoparticles[J].Composites Science and Technology,2010,71(4):471-479. |
| [12] | Zhang H,Zhang Z,Friedrich K,et al.Property improvements of in situ epoxy nanocomposites with reduced interparticle distance at high nanosilica content[J].Acta Materialia,2006,54(7):1833-1842. |
| [13] | Zhang H,Tang L C,Zhang Z,et al.Fracture behaviours of in situ silica nanoparticle-filled epoxy at different temperatures[J].Polymer,2008,49(17):3816-3825. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%