The erosion resistance tests were used to research the erosion wear behavior of CaO-Al2O3-SiO2 system glass-ceramic. With the orthogonal test method, the factors that affect the erosion wear of CaO-Al2O3-SiO2 system glass-ceramic such as particles property, impact angle, impact time, size of particles were discussed.The results show that erosion rate rises along a straight line at the early period of erosion wear.With the impact time increased,the erosion rate deviates from original staight line,tendency of the erosion rate increases.With the size of paricle increased,it will have more kinetic energy,the erosion rate of the surface of glass-ceramics ploate rises.
参考文献
| [1] | Gutman R .Thermal Technologies to Convert Solid Waste Residuals into Technical Glass Products[J].Glass Science and Technology,1996,96:285-289. |
| [2] | Pannhorst W .Glass ceramics: state-of-the-art[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1997(0):198-204. |
| [3] | Alanyali H;Rawlings RD;RogersP S .Development of Bioactive Apoceram Glass Ceramics[J].British Ceramic Transactions,1988,97:240-246. |
| [4] | N I Min'ko .Decorative Glass Ceramic Materials Simulating Semiprecious Stones[J].Glass and Ceramics,1998,55(78):243-250. |
| [5] | M Tanaka .β-Wollastonite Precipitated Glass Ceramic Synthesized from Waste Granite[J].Journal of the Ceramic Society of Japan,1999,107(07):627-632. |
| [6] | Barbieri;A M Ferrari;I Lancellotti;C Leonelli, J M Rincon MRomero .Crystallisation of(Na2O-MgO)-CaO-Al2O3-SiO2 Glass System Formulated from Waste Products[J].Journal of the American Ceramic Society,2000,83(10):2515-2520. |
| [7] | Zhao Qian;Cheng Jinshu;Wang Huaide;Yuan Jian .RESEARCH ON FACTORS AFFECTING THE COLOURATION OF RED GLASS-CERAMICS[J].Journal of Wuhan University of Technology.Materials Science edition,1996(3):46-52. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%