以CSP流程生产的35W440无取向电工钢热轧板为研究对象,研究了不同退火温度对无取向电工钢磁性能的影响规律.研究的结果表明,在实验参数的范围内,随着退火温度的升高,最终成品的晶粒尺寸增大.利用X射线测量了不同退火温度的成品板的宏观织构,结果表明,退火温度的提高有利于减弱{111}面织构,从而有利于改善产品磁性能的α纤维织构和{100}〈0vw〉有利织构组分得到了增强.因此随着退火温度的提高,成品板试样的铁损降低,磁感增加.
参考文献
| [1] | 何忠治 .电工钢的现状与展望[J].钢铁研究学报,2001,53(04):4-l5. |
| [2] | Kocks U F.Texture and Anisotropy:Preferred Orientations in Polycrystals and their Effect on Materials Properties[M].New Yorkambridge UniversityPress,1998 |
| [3] | Jong-Tae PARK;Jerzy A. SZPUNAR .Texture Development during Grain Growth in Nonoriented Electrical Steels[J].ISIJ International,2005(5):743-749. |
| [4] | Marco A. da Cunha;Sebastiao C. Paolinelli .Effect of the annealing temperature on the structure and magnetic properties of 3 percent Si non-oriented steel[J].Journal of Magnetism and Magnetic Materials,2003(0):379-381. |
| [5] | 毛卫民;杨平;陈冷.材料织构分析原理与检测技术[M].北京:冶金工业出版社,2008:29. |
| [6] | Jong-Tae Park;Jerzy A. Szpunar .Evolution of recrystallization texture in nonoriented electrical steels[J].Acta materialia,2003(11):3037-3051. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%