The influence of melt superheating treatment on the solid/liquid （S/L） interface morphology of directionally solidified Ni-based superalloy DZ125 is investigated to elucidate the relationship between melt characteristic and S/L interface stability. The results indicate that the interface morphology is not only related to the withdrawal velocity （R） but also to the melt superheating temperature （Ts） when the thermal gradient of solidification interface remains constant for different Ts with appropriate superheating treatment regulation. The interface morphology changes from cell to plane at R of 1.1 μm/s when Ts increases from 1500°C to 1650°C, and maintains plane with further elevated Ts of 1750°C. However, the interface morphology changes from coarse dendrite to cell and then to cellular dendrite at R of 2.25 μm/s when Ts increases from 1500°C to 1650°C and then to 1750°C. It is proved that the solidification onset temperature and the solidification interval undergo the nonlinear variation when Ts increases from 1500°C to 1680°C, and the turning point is 1650°C at which the solidification onset temperature and the solidification interval are all minimum. This indicates that the melt superheating treatment enhances the solidification interface stability and has important effect on the solidification characteristics.
参考文献
| [1] | L. Liu;T.W. Huang;J. Zhang .Microstructure and stress rapture properties of single crystal superalloy CMSX-2 under high thermal gradient directional solidification[J].Materials Letters,2007(26):227-230. |
| [2] | F.Long,Y.S.Yoo,S.M.Seo,T.Jin,Z.Q.Hu,C.Y.Jo.Effect of Re Addition and Withdrawal Rate on the Solidification Behavior of Directionally Solidified Superalloy AM3[J].材料科学技术学报（英文版）,2011(02):101-106. |
| [3] | H. Fredriksson;E. Fredriksson .A model of liquid metals and its relation to the solidification process[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(0):455-459. |
| [4] | F. S. Yin;X. F. Sun;J. G. Li;H. R. Guan;Z. Q. Hu .Effect of melt treatment on the cast structure of M963 superalloy[J].Scripta materialia,2003(4):425-429. |