本文采用微乳-水热法一步合成了核壳型TiO2/Al2O3纳米粉体.通过对产物的Zeta电位研究得出制备Ti(OH)4/Al(OH)3核壳前驱体的最佳pH值.并且采用XRD、TEM及SEM等表征方法与普通一步水热法合成的TiO2/Al2O3纳米粉体的晶形晶貌进行比较.结果表明:微乳-水热法能改善颗粒形状和大小,产品的颗粒大小均匀、平均晶粒粒径为13.68 nm.
参考文献
| [1] | 崔爱莉,王亭杰,金涌,孙牧.二氧化钛表面包覆氧化硅纳米膜的热力学研究[J].高等学校化学学报,2001(09):1543-1545. |
| [2] | Jain S;Fotuo G P .Theoretical study on gas-phase coating of aerosol particles[J].Journal of Colloid and Interface Science,1997,1(01):26. |
| [3] | 崔爱莉,王亭杰,金涌,肖帅刚,盖旭东.TiO2表面包覆SiO2和Al2O3的机理和结构分析[J].高等学校化学学报,1998(11):1727-1729. |
| [4] | Boutonnet M;Kizling J;Stenius P .The preparation of monodisperse colloidal metal particles from microemulsions[J].Colloids and Surfacec,1982,5(03):209-225. |
| [5] | 杨传铮;谢达材;陈癸尊.物相衍射分析[M].北京:冶金工业出版社,1989 |
| [6] | Derjaguin B V .A theory of the heterocoagulation,interaction and adhesion of dissimilar particles in solutions of electrolytes[J].Discussions of the Faraday Society,1954,18:85-98. |
| [7] | Hogg R;Healy T W .Summarizing remarks,colloid stability[J].Discussions of the Faraday Society,1966,42:317-321. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%