通过室温拉伸、疲劳裂纹扩展速率测试及透射电镜等实验手段,研究Mg含量对Al-Cu-Mg-Ag合金时效析出过程与力学性能的影响.结果表明:随着Mg含量的增加,合金的时效响应速率加快,而强度则先上升后下降,当Cu/Mg比为6时,合金强度最高;Mg含量的提高为主要析出相Ω相提供了更多的形核位置,使得合金基体中的析出相细小弥散,分布均匀;Cu/Mg比接近4的合金经165 ℃时效30 min处理后,晶内析出大量的Cu-Mg原子团簇,疲劳性能最佳.
参考文献
| [1] | Polmear I J;Couper M J .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,19(04):1027. |
| [2] | Vietzj T;Polmear I J .[J].Journal of the Institute of Metals,1966,94(12):410. |
| [3] | Knowles K M;Stobbs W M .[J].Acta Crystallographica Section B:Structural Science,1988,B44:207. |
| [4] | Murayama M;Hono K .[J].Scripta Materialia,2001,44(04):701. |
| [5] | Abis S;Mengucci P;Riontino G .[J].PHILOSOPHICAL MAGAZINE B-PHYSICS OF CONDENSED MATTER STATISTICAL MECHANIC,1993,67(04):465. |
| [6] | Teleshov V V;Kaputkin E Ya;Golovleva A P et al.[J].Metal Science and Heat Treatment,2005,47(3-4):139. |
| [7] | Mukhopadhyay A K .[J].Materials Transactions-Japan Institute of Metals,1997,38(05):478. |
| [8] | Hutchinson C R;Fan X et al.[J].Acta Materialia,2001,49:2827. |
| [9] | Ringer S P;Hono K;Polmear I J et al.[J].Acta Materialia,1996,44(05):1883. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%