通过硬度测试、韧性试验和显微组织比较,在不同的工艺条件下,对比研究了两步法和传统的单步法等温淬火工艺条件下得到的等温淬火球铁(ADI)的组织和性能.结果表明,采用"低温285℃保温形核+高温340℃或370℃等温淬火"的两步法等温淬火工艺与传统的340℃或370℃单步法等温淬火工艺相比,两步法得到的ADI比传统的单步法得到的ADI试样微观组织更细化、硬度显著提高、韧性也有了明显的改善.
参考文献
[1] | J. Zimba;D.J. Simbi;E. Navara .Austempered ductile iron: an alternative material for earth moving components[J].Cement & concrete composites,2003(6):643-649. |
[2] | Sidjanin L;Novovie M;Smallman R E .Metallographic investigations of ADI materials[J].Praktische Metallographie,1996,33(01):2-16. |
[3] | Voigt R C .Austempered ductile iron-processing and properties[J].Cast Metals,1989,2(02):71-93. |
[4] | 刘建伟;郝社平.美国康明斯B系列柴油发动机奥贝球铁齿轮的研究应用[J].现代铸铁,1999(03):73-76. |
[5] | Kovacs B V .Heat treating of austempered ductile iron[J].AFS Transactions,1997,74:501-505. |
[6] | Yang J H;Putatunda S K .Influence of a new two-step austempering process on strain-harding behavior of atmtempered ducti|e iron (ADI)[J].Materials Science and Engineering A,2004,382:265-279. |
[7] | Yang J H;Putatunda S K .Improvement in strength and toughness of austempered ductile cast iron by a novel two-step austempering process[J].Materials & Design,2004,25:219-230. |
[8] | Putatunda S K .Develepment of austempered ductile cast iron with simultaneous high yield strength and fracture toughness by a novel two-step austempering process[J].Materials Science and Engineering A,2001,315:70-80. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%