通过X射线衍射及磁测量手段研究了Gd2Fe14Cr3化合物的热膨胀性质及本征磁致伸缩性质.研究结果表明,Gd2Fe14Cr3化合物在294～692K范围内,具有单相的Th2Zn17型菱方相结构;磁测量的研究结果表明,Gd2Fe014Cr3化合物的居里温度约为540K,比其母合金Gd2Fe17高约30K;在452～512K温度范围内Gd2Fe14Cr3化合物具有负热膨胀性质,其热膨胀系数为-1.6×10-5/K;对本征磁致伸缩的研究结果表明,Gd2Fe14Cr3化合物中存在着较强的各向异性的本征磁致伸缩,而且由实验数据可以看出对体磁致伸缩的贡献主要发生在c轴上.
参考文献
| [1] | Wang C;WangT M;Sheng R et al.[J].Physica,2001,30:772. |
| [2] | Hao Y M;Zhang Y Y;Jiang X Y et al.[J].Chinese Physics Letters,2009,269:026501. |
| [3] | Hao Y M;He X H;An L Q et al.[J].Chinese Physics Letters,2008,25:66. |
| [4] | Hao YM;Zhao M;Zhou Y;Hu JF .Negative thermal expansion and spontaneous volume magnetostriction of Tb2Fe16Cr compound[J].Scripta materialia,2005(3):357-360. |
| [5] | Hao Y M;Zhou Y;Zhao M .[J].Acta Physica Sinica,2005,5:337. |
| [6] | Hao Y M;Zhao M;Zhou Y .[J].Journal of Applied Physics,2005,8:125. |
| [7] | Narasimhn K S V L;Wallace W E;Hutchers R D .[J].IEEE Transactions on Magnetics,1974,10:729. |
| [8] | Hao Y M;Zhang P L;Zhang J X et al.[J].Journal of Physics: Condensed Matter,1996,81:321. |
| [9] | Hao Shiqiang;Chen Nanxian;Jiang Shen .[J].Surface Science,2008,602(01):46. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%