纵观当前混凝土结构使用寿命预测模型的研究,分别从基于碳化的寿命预测模型、基于氯离子扩散导致钢筋锈蚀的寿命预测模型及基于混凝土损伤的寿命预测模型3方面介绍了该领域的研究进展,提出在实际使用期内,结构往往要经历小修、中修或大修使得结构可靠度相应提高或结构劣化速度减缓,因此建筑结构的寿命预测还应考虑维修历史和效果.
参考文献
| [1] | 陈肇元.混凝土结构的耐久性设计方法[J].建筑技术,2003(05):328-333. |
| [2] | Clifton J R .Predicting the service life of concrete[J].ACI Materials Journal,1993,90(06):611. |
| [3] | 金伟良.混凝土结构耐久性[M].北京:科学出版社,2002:24. |
| [4] | 牛荻涛.混凝土结构耐久性与寿命预测[M].北京:科学出版社,2003:10. |
| [5] | 许丽萍;黄士元.预测混凝土中碳化深度的数学模型[J].上海建材学院学报,1991(04):10. |
| [6] | Papadakis V G;Vayenas G;Fardis M N .Fundamental modeling and experimental investigation of concrete carbonation[J].ACI Materials Journal,1991,88:363. |
| [7] | 刘志勇,孙伟.多因素作用下混凝土碳化模型及寿命预测[J].混凝土,2003(12):3-7. |
| [8] | Song H W;Kim H J;Kwon S J.Prediction of service life in cracked reinforced concrete structures subjected to chloride attack and carbonation[A].,2005:767. |
| [9] | 刘志勇 .基于环境的海工混凝土耐久性试验与寿命预测方法研究[D].东南大学,2006. |
| [10] | 金祖权 .西部地区严酷环境下混凝土的耐久性与寿命预测[D].东南大学,2006. |
| [11] | 蒋金洋,孙伟,金祖权,王彩辉.疲劳载荷与碳化耦合作用下结构混凝土寿命预测[J].建筑材料学报,2010(03):304-309. |
| [12] | 洪定海.混凝土中钢筋的腐蚀与保护[M].北京:中国铁道出版社,1998 |
| [13] | A.Boddy;E.Bentz .An overview and sensitivity study of a multimechanistic chloride transport model[J].Cement and Concrete Research,1999(6):827-837. |
| [14] | Amey S L;Johnson D A;Miltenberger M A .Prediction service life of concrete marine structure:An environment methodology[J].ACI Structural Journal,1998,95(02):205. |
| [15] | 余红发,孙伟,鄢良慧,麻海燕.混凝土使用寿命预测方法的研究Ⅰ--理论模型[J].硅酸盐学报,2002(06):686-690. |
| [16] | 余红发,孙伟,麻海燕,鄢良慧.混凝土使用寿命预测方法的研究Ⅱ--模型验证与应用[J].硅酸盐学报,2002(06):691-695. |
| [17] | 余红发,孙伟,麻海燕,鄢良慧.混凝土使用寿命预测方法的研究Ⅲ--混凝土使用寿命的影响因素及混凝土寿命评价[J].硅酸盐学报,2002(06):696-701. |
| [18] | Prezzi M;Geyskens P;Monteiro J M .Reliability approach to service life prediction concrete exposed to marine environment[J].ACI Materials Journal,1996,93(06):544. |
| [19] | Michacl P. Enright;Dan M. Frangopol .Probabilistic analysis of resistance degradation of reinforced concrete bridge beams under corrosion[J].Engineering structures,1998(11):960-971. |
| [20] | Stewart M G;Rosowsky D V.Time-dependent reliability of deteriorating reinforced concrete bridge decks[J].Structural Safety,1998(20):91. |
| [21] | Cheung M S;Kyle B R .Service life prediction of concrete structures by reliability analysis[J].Construction and Building Materials,1996,10(01):45. |
| [22] | Peter Schiessl;Christoph Gehlen.New approach of service life design for constructure[A].山东青岛,2005:9. |
| [23] | 李田;刘西拉.混凝土结构耐久性分析与设计[M].北京:科学出版社,1999 |
| [24] | Atkinson A;Hearne J A.Mechanistic model for the durability of concrete barriers exposed to sulfate-bearing groundwater[A].,1990:149. |
| [25] | Gerdes A;Wittmann F H.Influence of stress corrosion on fracture energy of cementitious materials[A].Freiburg:AEDIFCATIO Publishers,1995 |
| [26] | Schneider U;Chen S W .The chemomechanical effect and the mechanochemical effect on high-performance concrete subjected to stress corrosion[J].Cement and Concrete Research,1998,28(04):509. |
| [27] | 关宇刚 .单一和多重破坏因素作用下高强混凝土的寿命评估[D].东南大学,2002. |
| [28] | 蒋金洋,孙伟,王晶,王彩辉.弯曲疲劳载荷作用下结构混凝土抗氯离子扩散性能[J].东南大学学报（自然科学版）,2010(02):362-366. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%