利用低共熔组成的0.38LiOH-0.62 LiNO3混合锂盐体系,与高密度前驱体掺杂Co的Ni(OH)2、TiO2粉末在低温下自混合,无需前期研磨和后续洗涤,直接制备出振实密度达3.17g/cm2的高密度锂离子电池正极材料LiNi0.8Co0.15Ti0.05O2.X射线衍射分析表明合成的LiNi0.8Co0.15Ti0.05O2具有规整的层状α-NaFeO2结构.扫描电镜显示产物颗粒均匀,电性能测试表明,在0.2C放电倍率和3.0～4.3V的电压范围内,LiNi0.8Co0.15Ti0.05O2良好首次放电比容量达169mAh/g,且具有良好的循环性能.
参考文献
| [1] | Chang C C;Kim J Y;Kim P N .[J].Journal of Power Sources,2000,89:56-63. |
| [2] | Yoshio M;Noguchi H;Itoh J et al.[J].Journal of Power Sources,2000,90:176-181. |
| [3] | Madhavi S;Subba G V;Chowdari B et al.[J].Journal of Power Sources,2001,93:156-162. |
| [4] | Kajiyama A;Takada K;Arihara K et al.[J].Journal of the Electrochemical Society,2003,150:157-160. |
| [5] | Croguenec L;Suard E;Willamann P et al.[J].Chemistry of Materials,2002,14:2149-2157. |
| [6] | Gao Y;Yakovleva M;Ebner W .[J].Electrochem and Solid State Letters,1998,1:117-119. |
| [7] | Bruno Scrosati .Recent advances in lithium ion battery materials[J].Electrochimica Acta,2000(15/16):2461-2466. |
| [8] | 常照荣,齐霞,吴锋,孙东,苗旺.镍系锂离子电池正极材料的合成工艺及改性研究[J].材料导报,2006(05):92-96. |
| [9] | 应皆荣,高剑,姜长印,万春荣,何向明.控制结晶法制备球形锂离子电池正极材料的研究进展[J].无机材料学报,2006(02):291-297. |
| [10] | Wang G X;Bradhurst J H .[J].Journal of Power Sources,2000,85:279-283. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%