采用聚乙二醇(PEG)和聚乙烯醇(PVA)分别对硅溶胶进行改性,并分析改性前后溶胶体系红外光谱、ち电位和溶胶粒径的变化,根据透光率的变化考察了溶肢体系的热稳定性;通过原位合成法制备了PET-SiO2和PET-SiO2-PVA杂化材料,并对其透光率进行了比较.结果表明,采用PVA改性SiO2溶胶既能有效地降低SiO2的粒径,又能抑制其在原住合成中的团聚;PET-SiO2-PVA透明度与唧-SiO2透明度相比略有提高,表明改性硅溶胶能在一定程度上抑制原位合成的聚对苯二甲酸乙二醇酯(PET)中SiO2的团聚.
参考文献
| [1] | Choi WJ;Kim HJ;Yoon KH;Kwon OH;Hwang CI .Preparation and barrier property of poly(ethylene terephthalate)/clay nanocomposite using clay-supported catalyst[J].Journal of Applied Polymer Science,2006(6):4875-4879. |
| [2] | Guan GH;Li CC;Zhang D .Spinning and properties of poly(ethylene terephthalate)/organomontmorillonite nanocomposite fibers[J].Journal of Applied Polymer Science,2005(6):1443-1447. |
| [3] | Tsai, TY;Li, CH;Chang, CH;Cheng, WH;Hwang, CL;Wu, RJ .Preparation of exfoliated polyester/clay nanocomposites[J].Advanced Materials,2005(14):1769-1772. |
| [4] | 刘海明,王锐,张大省.PET/无机纳米粒子复合物的制备及性能[J].合成纤维工业,2006(03):15-17. |
| [5] | Liu WT.;Tian XY.;Cui P.;Li Y.;Zheng K.;Yang Y. .Preparation and characterization of PET/Silica nanocomposites[J].Journal of Applied Polymer Science,2004(2):1229-1232. |
| [6] | 王孝龙,纪全,孔庆山,夏延致.PET/SiO2纳米复合材料的燃烧性能研究[J].合成技术及应用,2007(02):7-10. |
| [7] | He JP;Li HM;Wang XY;Gao Y .In situ preparation of poly(ethylene terephthalate)-SiO2 nanocomposites[J].European Polymer Journal,2006(5):1128-1134. |
| [8] | 王娜,乔生儒,杨斌.PET/纳米SiO2复合体系结晶性和SiO2粒子分散性研究[J].材料导报,2006(z1):200-202,205. |
| [9] | 赵虹.含氧化合物的红外光谱特征[J].光谱学与光谱分析,2001(04):506-507. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%