运用激光熔覆技术在16Mn钢表面制备了钴基合金涂层(Co55)、含20%SiCp(体积分数,下同)的钴基合金涂层(CoSiC)以及含20%B4Cp钴基合金涂层(CoB4C),比较研究了合金涂层的组织、相结构、显微硬度及滑动磨损性能.结果表明: 合金涂层由涂层结合区的胞状共晶组织及涂层区的树枝状亚共晶组织组成,CoSiC涂层及CoB4C涂层的树枝晶比Co55涂层的更细小; B4Cp及SiCp在熔覆过程中完全熔解,其分解出的B,C,Si与涂层中的合金元素结合形成了更多的化合物,Co55涂层由γ-Co和(Cr,Fe)7C3组成,CoSiC涂层由γ-Co,Cr7C3,Cr23C6,CoSi2,Cr3Si和Si2W组成,CoB4C涂层由γ-Co,Cr7C3,Cr23C6,CrB,CrB2和Fe23(C,B)6组成; 3种激光熔覆涂层的显微硬度及耐磨性由高到低的顺序为CoB4C→CoSiC→Co55.对涂层的强化机理进行了分析.
参考文献
| [1] | 张松,张春华,康煜平,吴维,王茂才,文交/力忠.钛合金表面激光熔覆原位生成TiC增强复合涂层[J].中国有色金属学报,2001(06):1026-1030. |
| [2] | 马乃恒,梁工英,苏俊义.激光熔覆工艺参数对TiCp/Al表层复合材料的影响[J].中国有色金属学报,2001(06):1041-1044. |
| [3] | Yang Y. .Microstructure and properties of laser-clad high-temperature wear-resistant alloys[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,1999(1/2):19-23. |
| [4] | 张松,张春华,孙泰礼,文力忠,吴维,王茂才.激光熔覆钴基合金组织及其抗腐蚀性能[J].中国激光,2001(09):860-864. |
| [5] | 曾大文,王毛球,谢长生.Co基合金激光熔覆层的局部组织特征[J].稀有金属材料与工程,1998(02):87-91. |
| [6] | Przybylowicz J;Kusinski J .Laser cladding and erosive wear of Co-Mo-Cr-Si coating[J].Surface and Coatings Technology,2000,125:13-18. |
| [7] | J. Przybylowicz;J. Kusinski .Structure of laser cladded tungsten carbide composite coatings[J].Journal of Materials Processing Technology,2001(1/2):154-160. |
| [8] | M. Riabkina-Fishman;E. Rabkin;P. Levin;N. Frage;M. P. Dariel;A. Weisheit;R. Galun;B. L. Mordike .Laser produced functionally graded tungsten carbide coatings on M2 high-speed tool steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1):106-114. |
| [9] | Wu Xiao-lei;HONG You-shi .Microstructure and mechanical properties at TiCp Ni-alloy interfaces in laser-synthesized coatings[J].Materials Science and Engineering A,2001,A318:15-21. |
| [10] | Q. Li;T. C. Lei;W. Z. Chen .Microstructural characterization of WCp reinforced Ni-Cr-B-Si-C composite coatings[J].Surface & Coatings Technology,1999(2/3):285-291. |
| [11] | 斯松华,袁晓敏,何宜柱,Je-Hyun Lee,Mark T.Lusk.激光熔覆镍基金属陶瓷涂层的组织性能研究[J].中国激光,2002(08):759-762. |
| [12] | 李强,陈彦斌,雷廷权,杨德庄,周玉.激光熔覆WCp/Ni-Cr-B-Si-C自熔合金复合涂层的显微结构及干滑动磨损[J].中国激光,1999(02):186. |
| [13] | 李玉红,张思玉,郑克全.不同扫描速度下A3钢表面B4C-TiN-Co激光组织和性能的研究[J].激光技术,1999(02):126. |
| [14] | 李强,雷廷权,王富耻,欧阳家虎,周玉.激光表面熔覆SiCp/Ni-Cr-B-Si-C涂层的组织演化及其相确定[J].中国激光,1999(01):80-84. |
| [15] | 陈传忠;于慧君;侯勇 .45钢表面激光熔覆WC/Co[J].陶瓷学报,1998,19(03):137-143. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%