采用全浸试验和动电位极化方法比较了四种不同的仿古铸铁在3.5%NaCl溶液中的腐蚀行为.结果表明,仿古灰口铸铁的腐蚀速率较仿古白口铸铁高;两种灰口铸铁中,低硫试样较高硫试样的腐蚀速率高,耐腐蚀性能差;两种白口铸铁中,低硫含量的试样与高硫含量的腐蚀速率和耐腐蚀性能均接近;X射线衍射仪分析表明四种铸铁的腐蚀产物均含有纤铁矿、磁铁矿和针铁矿,其中疏松不稳定的纤铁矿含量最多,并未发现海水打捞铁器中常见的腐蚀产物-四方纤铁矿.
The corrosion behavior of four kind of cast irons made according to the composition of several ancient cast irons in 3.5%NaCl solution were investigated by using immersion test and potentiodynamic polarization measurement.The results showed that the corrosion rate of the grey cast irons was higher than that of the white cast irons.The grey iron with low sulfur content showed a higher corrosion rate and poor corrosion resistance in comparison with that with high sulfur;but for the white irons,the sulfur content showed no significant effect on their corrosion properties.XRD spectra analysis indicated that lepidocrocite,magnetite and goethite existed in the corrosion products of all four cast irons,among which the loose,unstable lepidocrocite was predominant.Akaganeite,the most commonly seen corrosion product for ironwares excavated from the sea,however,had not been seen among the examined corrosion products.
参考文献
[1] | 华觉明,中国古代钢铁技术的特色及其形成[A].华觉明等著.中国冶铸史论集[C].北京:文物出版社,1986. |
[2] | 中国腐蚀与防护学会主编.自然环境的腐蚀与防护大气·海水·土壤[M].北京:化学工业出版社,1996. |
[3] | Gilberg M R, Seeley N J. The identity of compounds con- taining chloride ions in marine iron corrosion products: a critical review[J]. Stud. Conserv., 1981, 26: 50. |
[4] | 陈俊明,蔡振月,王志杰等.铁锈物理化学(I)穆斯堡尔内转换电子谱研究取白海水的低合金钢上的阻挡层铁锈[J].中国腐蚀与防护学报,1982,2(2):1. |
[5] | 陈俊明,王志杰,蔡振月等.铁锈物理化学II穆斯堡尔内转换电子谱研究低合金钢在模拟海水中的阻挡层铁锈[J].中国腐蚀与防护学报,1982,2(2):10. |
[6] | Ouyang W Z, Xu C C. Studies on the localized corro- sion and desalination treatment of simulated cast iron ar- tifact[J]. Stud. Conserv., 2005, 50(2):101. |
[7] | JB/T7901-1999,中华人民共和国机械行业标准《金属材料实验室均匀腐蚀全浸试验方法》[S]. |
[8] | 夏兰廷,黄桂桥,张三平等.金属材料的海洋腐蚀与防护[M].北京:冶金工业出版社,2003. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%