The austempering after hot rolling in hot rolled Si-Mn TRIP (transformation-induced plasticity) steels was investigated. The mechanism of TRIP was discussed through examination of the microstructure and the mechanical properties of this kind of steel. The results showed that the strain-induced transformation to martensite of retained austenite occurs in hot rolled Si-Mn TRIP steels. The sample exhibited a good combination of ultimate tensile strength and total elongation when it was held at the bainite transformation temperature after hot deformation. The stability of retained austenite increases with an increase in isothermal holding time, and a further increase in the holding duration resulted in the decrease of stability. The mechanical properties were optimal when holding for 25 min, and tensile strength and total elongation reached the maximum values (774 MPa and 33%,respectively).
参考文献
| [1] | Zackay V F;Parker E R;Fahr D .The Enhancement of Ductility on High-Strength Steels[J].Transactions ASM,1967,60:252-259. |
| [2] | Sakuma Y;Matsumura O;Takechi H .Mechanical Properties and Retained Austenite in Intercritically Heat-Treated Bainite-Transformed Steel and Their Variation With Si and Mn Additions[J].Metallurgical and Materials Transactions,1991,22A(02):489-498. |
| [3] | Sugimoto K I;Misu M;Kobayashi M .Effects of Second Phase Morphology on Retained Austenite Morphology and Tensile Properties in a TRIP-Aided Dual-Phase Steel Sheet[J].ISIJ International,1993,33:775-782. |
| [4] | Sugimoto K I;Kobayashi M;Hashimoto S I .Ductility and Strain-Induced Transformation in a High-Strength Transformation-Induced Plasticity-Aided Dual-Phase Steel[J].Metallurgical and Materials Transactions,1992,23A(11):3085-3091. |
| [5] | M. De MEYER .The Influence of the Substitution of Si by Al on the Properties ofCold Rolled C-Mn-Si TRIP Steels[J].ISIJ International,1999(8):813-822. |
| [6] | A. Zarei HANZAKI;P. D. HODGSON;S. YUE .Hot Deformation Characteristics of Si-Mn TRIP Steels with and without Nb Microalloy Additions[J].ISIJ International,1995(3):324-331. |
| [7] | E. V. Pereloma;I. B. Timokhina;P. D. Hodgson .Transformation behaviour in thermomechanically processed C-Mn-Si TRIP steels with and without Nb[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(0):448-452. |
| [8] | Akihiko KOJIMA;Yoshiyuki WATANABE;Yoshio TERADA;Atsuhiko YOSHIE;Hiroshi TAMEHIRO .Ferrite Grain Refinement by Large Reduction per Pass in Nonrecrystallization Temperature Region of Austenite[J].ISIJ International,1996(5):603-610. |
| [9] | Rassoul P;Steve Y .Dynamic Transformation of Austenite to Ferrite in Low Carbon Steel[J].ISIJ International,1994,34(03):270-290. |
| [10] | J. MAHIEU;J. MAKI;B.C. De COOMAN .Phase Transformation and Mechanical Properties of Si-Free CMnAl Transformation-Induced Plasticity-Aided Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2002(8):2573-2580. |
| [11] | Zhuang Li;D. WU .Effects of hot deformation and subsequent austempering on the mechanical properties of Si-Mn TRIP steels[J].ISIJ International,2006(1):121-128. |
| [12] | Koh-ichi SUGIMOTO .Effects of Retained Austenite Parameters on Warm Stretch-flangeability in TRIP-aided Dual-phase Sheet Steels[J].ISIJ International,1999(1):56-63. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%