通过采用羟基硅油对炭黑表面修饰, 改善炭黑与硅橡胶之间的相容性, 从而减小炭黑与硅橡胶界面热阻, 制备了高导热系数炭黑填充硅橡胶, 研究了炭黑填料与硅橡胶的相容性及炭黑/硅橡胶的导热系数。结果表明： 与原炭黑/硅橡胶体系相比, 经过羟基硅油修饰的炭黑与硅橡胶的相容性得到明显改善。当经表面修饰炭黑的质量分数为36.59%时, 表面修饰炭黑/硅橡胶的导热系数可达到0.591 W·（m·K）^-1, 较同含量未修饰炭黑/硅橡胶的导热系数高38.7%。
Carbon black (CB) was modified with hydroxyl silicone oil to improve the compatibility between CB and silicone rubber (SR), which resulted in diminishing the thermal interfacial resistance between CB and silicone rubber, for preparing CB/SR composites with high thermal conductivity. The compatibility between CB and SR, as well as the thermal conductivity of the CB/SR composites was investigated. The results show that the surface modified CB has a better compatibility with silicone rubber compared with the origin CB. When the loading of the modified CB was 36.59%, the thermal conductivity of the modified CB/SR composites can be as high as 0.591 W·(m·k)^-1, 38.7% higher than that of the origin CB/SR composites with the same loading.
参考文献
| [1] | Barea R, Belmonte M, Osendi M I, Miranzo P. Thermal conductivity of A1203/SiC platelet composites[J]. Journal of the European Ceramic Society, 2003, 23- 1773-1778. |
| [2] | 乔梁,赵洪强,郑精武,姜力强.片状A120s对A120./FEP复合材料热导率的影响[J].复合材料学报,2009,26(6):37-41. |
| [3] | Zhou Wenying, Qi Shuhua, Li Haidong, Shao Shiyu. Study on insulating thermal conductive BN/HDPE composites [J].Thermochimica Acta, 2007, 452(1): 36-42. |
| [4] | Yu Aiping, Ramesh P, Sun Xiaobo, Bekyarova E, et al. Enhanced thermal conductivity in a hybrid graphite nanoplate- carbon nanotube filler for epoxy composites[J]. Advanced Materials, 2008, 20(24): 4740-4744. |
| [5] | 周文英,齐暑华,王彩风,郭建.高温导热绝缘涂料[J].复合材料学报,2007,24(2):28-32. |
| [6] | Thostenson E T, Chou T W. Processing structure- multi- functional property relationship in carbon nanotube/epoxy composites[J].Carbon, 2006, 44(14): 3022-3029. |
| [7] | 费海燕,朱鹏,宋艳江,等.石墨和碳纤维分别改性热塑性聚酰亚胺复合材料的导热行为[J].复合材料学报,2007,24(5):44-49. |
| [8] | Liu C H, Fan S S. Effects of chemical modifications on the thermal conductivity of carbon nanotube composites [J ].Applied Physics Letter, 2005, 86: 123106. |
| [9] | Ganguli S, Roy A K, Anderson D P. Improved thermal conductivity for chemically funetionalized exfoliated graphite/ epoxy composites [J].Carbon, 2008, 46(5): 806-817. |
| [10] | Shenogin S, Bodapati A, Xue L, Ozisik R, Keblinski P. Effect of chemical functionalization on thermal transport of carbon nanotube composites [J]. Applied Physics Letter, 2004, 85: 2229-2231. |
| [11] | 李海涛,何燕,马连湘.炭黑填充天然橡胶复合材料热导率的研究[J].青岛科技大学学报,2009,30(3):256-258. |
| [12] | Nasr G M, Badawy M M, Gwaily S E, Shash M N, Hassan H H. Thermophysical properties of butyl rubber loaded with different types of carbon black [J]. Polymer Degradation and Stability, 1995, 48(2): 237-241. |
| [13] | Peters J E, Papavassiliou D V, Grady B P. Unique thermal conduetivity behavior of single- walled carbon nanotube polystyrene composites [J].Macromolecule, 2008, 41 (20) 7274-7277. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%