为提高纳米TiO_2的可见光催化活性,采用沉淀-浸渍法制备了一种新型Ni和S共掺杂TiO_2纳米复合光催化剂.通过紫外-可见(UV-Vis-)漫反射、X-射线衍射(XRD)、透射电子显微镜(TEM)和X-荧光(EDX)等手段对其结晶形态、晶粒尺寸、元素掺杂量和吸光性能等进行了表征.结果显示,催化剂Ni/S/TiO_2为锐钛矿晶相,平均粒径约为6～7 nm,比表面积高达260.42 m~2/g,感光范围可拓展到可见光区,且与纯TiO_2,S掺杂TiO_2和Ni掺杂TiO_2相比,光催化剂Ni/S/TiO_2的颗粒粒径更小,比表面积更大,光吸收边红移程度更显著.以活性艳蓝198染料溶液为模拟废水,以氙光灯为光源,对光催化剂Ni/S/TiO_2的催化活性进行了评价.结果表明,Ni/S/TiO_2具有比纯TiO_2、S掺杂TiO_2和Ni掺杂TiO_2更高的可见光催化活性,氙光灯照射120 min,活性艳蓝198降解率可达到98.5%.
In order to improve visible light photocatalytic activities of nanometer TiO_2,a novel Ni/S/TiO_2nanocomposition photocatalyst was prepared by precipitation-doping method.The optical characteristics,crystal and particle size of Ni/S/TiO_2 photocatalyst were characterized by UV-Vis diffuse reflection spectra (DRS),X-ray diffraction(XRD),transmission electron microscopy(TEM)and energy dispersive X-ray fluorescence((DX).Results indicate that the Ni/S/TiO_2 photocatalyst is anatase phase,its particle size is about 6～7 nm,its specific surface area is about 260.42 m~2/g,and its absorption edge shifts to the visible light region.Compared with pure TiO_2,S-doped TiO_2 and Ni-doped TiO_2,the sizes of Ni/S/TiO_2 are smaller,its specific surface area is larger,and its absorption edge shifts more remarkably toward longer wavelength.The photocatalytic activities of Ni/S/TiO_2 were evaluated using the photodegradation of reactive blue 198 as probe reaction under the irradiation of xenon light.The Ni/S/TiO_2 photocatalyst shows higher photocatalytic activity than pure TiO_2,S-doped TiO_2 and Ni-doped TiO_2.The degradation rate of reactive blue 198 reaches 98.5%under the irradiation of Xe light lamp for 120 min.
参考文献
| [1] | 姜洪泉,王鹏,线恒泽,于凯.Zn2+掺杂TiO2纳米粉体的结构特性及光催化活性[J].哈尔滨工业大学学报,2007(08):1270-1275. |
| [2] | 孙尚梅,庞广生,李春光,黄玉亮,冯守华.熔盐中熟化处理提高BiFeO3的可见光催化活性[J].高等学校化学学报,2007(10):1830-1832. |
| [3] | 朱良俊,崔玉民.功能材料二氧化钛光催化反应活性的研究[J].材料科学与工艺,2007(06):876-880. |
| [4] | 刘守新,陈孝云,陈曦.酸催化水解法制备可见光响应N掺杂纳米TiO2催化剂[J].催化学报,2006(08):697-702. |
| [5] | Teruhisa Ohno;Miyako Akiyoshi;Tsutomu Umebayashi;Keisuke Asai;Takahiro Mitsui;Michio Matsumura .Preparation of S-doped TiO_2 photocatalysts and their photocatalytic activities under visible light[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2004(1):115-121. |
| [6] | Wei Zhao;Wanhong Ma;Chuncheng Chen;Jincai Zhao;Zhigang Shuai .Efficient Degradation of Toxic Organic Pollutants with Ni_2O_3/TiO_(2-x)B_x under Visible Irradiation[J].Journal of the American Chemical Society,2004(15):4782-4783. |
| [7] | 孙红旗,程友萍,金万勤,徐南平.镧、碳共掺杂TiO2的制备及其可见光催化性能[J].化工学报,2006(07):1570-1574. |
| [8] | 朱建,杨俊,陈麟,曹勇,戴维林,范康年.低温苯甲醇醇解法制备高活性锐钛矿型纳米晶TiO2光催化剂[J].催化学报,2006(02):171-177. |
| [9] | 崔玉民,范少华,苏凌浩.功能材料二氧化钛光催化降解酸性黑染料[J].北京科技大学学报,2006(07):625-629. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%